Three-dimensional matrices of structured porous monetite for tissue engineering and bone regeneration, and method of the preparation thereof
The present invention is comprised within tissue engineering and, specifically, within bone regeneration. The invention relates to a porous three-dimensional matrix of monetite which is biocompatible, has structured porosity and is predefined and reabsorbable, as well as to the method of synthesis capable of producing said material and the applications thereof. These matrices are a perfect base for cell colonization and proliferation, allowing the application thereof in tissue engineering and bone regeneration as a result of their advantageous properties of biocompatibility, reabsorption, osteoinduction, revascularization, etc.
1. A composition for bone structure regeneration, wherein said composition comprises a plurality of three-dimensional matrices of monetite with structured porosity, wherein said matrices contain vertical cylindrical channels which longitudinally traverse each matrix from one end to the other, wherein all of the channels that longitudinally traverse each matrix are uniformly-sized cylindrical macropores that are uniformly separated from one another by 0.5 mm ±60μm, said macropores having a diameter of 500μm ±60μm, and wherein in each matrix, none of said cylindrical macropores are connected to each other via another macropore contained within said matrix;
wherein said matrices are cylinders with a base diameter between 2 and 15 mm and a height between 1 and 5 mm, and have a perimetric area from said cylinder edge towards the center thereof of at least 0.5 mm which is free of macropores.
2. The composition of claim 1 , wherein the monetite content of the matrices is at least 90%.
3. The composition of claim 2 , wherein the monetite content of the matrices is 95%.
4. The composition of claim 2 , wherein the monetite content of the matrices is 100%.
5. The composition of claim 1 , wherein said matrices are obtained by heat-transforming a precursor material.
6. The composition of claim 5 , wherein the precursor material which is heat-transformed into monetite consists of a mixture of a solid phase formed by basic calcium phosphates, acidic calcium phosphates, a pore-inducing agent and a retarder which is set by adding distilled water.
7. The composition of claim 6 , wherein the molar ratio of basic phosphate/acidic phosphate is 1.6-1.8, the concentration of pore-inducing agent is 1-20% by weight, that of retarder is between 0.4-0.6% by weight and the (P/L) powder-liquid ratio of the monetite matrix is 3.
8. The composition of claim 7 , wherein the molar ratio of basic phosphate/acidic phosphate is 1.785, the concentration of pore-inducing agent is 3-10% by weight and that of retarder is 0.54% by weight.
9. The composition of claim 5 , wherein the acidic calcium phosphate is monocalcium phosphate, the basic calcium phosphate is beta-tricalcium phosphate, the pore-inducing agent is calcium carbonate and the retarder is sodium pyrophosphate.
10. The composition of claim 5 , wherein the precursor material is Brushite.
11. The composition of claim 1 , wherein said three-dimensional matrices are obtained from Brushite.
12. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 10 mm, a height of 5 mm, and 64 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
13. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 10 mm, a height of 3 mm, and 64 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
14. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 8 mm, a height of 5 mm, and 39 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
15. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 8 mm, a height of 3 mm, and 39 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
16. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 7 mm, a height of 5 mm, and 28 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
17. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 7 mm, a height of 3 mm, and 28 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards the center thereof which is free of macropores.
18. The composition of claim 11 , wherein said matrices are cylinders with a base diameter of 5 mm, a height of 3 mm, and 12 cylindrical macropores, respecting a perimetric area of 0.5 mm from said cylinder edge towards center thereof which is free of macropores.
19. The composition of claim 1 , wherein said matrices further comprise cells.
20. The composition of claim 19 , wherein said cells are mesenchymal cells, osteoblasts, osteoclasts, osteocytes, endothelial cells or combinations thereof.