Depth filter layer with inorganic layer double hydroxide

1. A depth filter layer, produced from

cellulose fibres and/or derivatives thereof,

at least one inorganic layer double hydroxide, and

at least one organic wet strength agent,

wherein the depth filter layer is produced from a mixture comprising a content by weight of the at least one inorganic layer double hydroxide of 10-65%, a content by weight of the cellulose fibres and/or derivatives thereof of 30-80% and a content by weight of the organic wet strength agent of 0.5-10%, based on the total weight of the mixture, and wherein the at least one organic wet strength agent reacts with carboxyl and/or OH groups of the cellulose fibres and/or derivatives thereof and the at least one inorganic layer double hydroxide to bridge components of the mixture to one another;

wherein the at least one inorganic layer double hydroxide comprises particles with an average diameter between 0.5 μm and 100 μm; and

wherein the depth filter layer is configured to bind nucleic acids adsorptively to the depth filter layer and to allow proteins to pass through the depth filter layer unimpeded.

2. The depth filter layer according to claim 1 , wherein the at least one inorganic layer double hydroxide contains monovalent alkali metal ions M + and/or divalent alkaline earth or transition metal ions M 2+ , trivalent main group or transition metal ions M 3+ , n-valent anions A n− with n=1-4 and hydroxide ions OH − .

3. The depth filter layer according to claim 2 , wherein the monovalent alkali metal ion M + is Li + , Na + , alone or in combination, the divalent alkaline earth or transition metal ion M 2+ is selected from the group of Mg 2+ , Sr 2+ , Ba 2+ , Ni 2+ , Cu 2+ , Co 2+ , Zn 2+ , Fe 2+ , Mn 2+ , Ca 2+ or combinations thereof, the trivalent main group or transition metal ion M 3+ is selected from the group of B 3+ , Al 3+ , Ga 3+ , Ni 3+ , Co 3+ , Cr 3+ , Fe 3+ , Mn 3+ , V 3+ , Ti 3+ , Sc 3+ , In 3+ or combinations thereof and the n-valent anion is selected from the group of F − , Cl − , Br − , I − , NO 3 − , ClO 4 − , ClO 3 − , IO 3 − , CO 3 2− , SO 4 2− , PO 4 3− , AsO 4 3− , S 2 O 3 2− , WO 4 2− , CrO 4 2− , [Fe(CN) 6 ] 3− , [Fe(CN) 6 ] 4− , [SiO(OH) 3 ] − , hetero polyacids, organic acids, organometallic complexes or combinations thereof.

4. The depth filter layer according to claim 1 , wherein the inorganic layer double hydroxide contains water of crystallization.

5. The depth filter layer according to claim 1 , wherein the inorganic layer double hydroxide has the formula

[(M 2+ ) 1-x (M 3+ ) x (OH) 2 ] x+ (A n− x/n )* m H 2 O

and that 0.1≦x≦0.5, 1≦n≦4 and m is a rational number including 0.

6. The depth filter layer according to claim 1 , wherein the inorganic layer double hydroxide has the formula

[(M + ) 1-x (M 3+ ) x (OH) 2 ] (2x-1)+ (A n− (2x-1)/n )* m H 2 O

and that 0.1≦x≦0.5, 1≦n≦4 and m is a rational number including 0.

7. The depth filter layer according to claim 1 , wherein the inorganic layer double hydroxide is hydrotalcite

Mg 6 Al 2 (CO 3 )(OH) 16 *4H 2 O.

8. The depth filter layer according to claim 7 , wherein hydrotalcite is not calcined.

9. The depth filter layer according to claim 1 , wherein the at least one organic wet strength agent is water-soluble and positively charged.

10. The depth filter layer according to claim 9 , wherein the at least one organic wet strength agent is selected from the group of polyamide/polyamine-epichlorohydrin resins, polyamide-epichlorohydrin resins, polyamine-epichlorohydrin resins, or mixtures thereof.

11. The depth filter layer according to claim 1 , wherein the depth filter layer is additionally produced with silicon dioxide and/or at least one derivative thereof.

12. The depth filter layer according to claim 1 , wherein the depth filter layer is additionally produced with kieselguhr or perlites or mixtures thereof.

13. The depth filter layer according to claim 11 , wherein the silicon dioxide and/or the at least one derivative comprises particles with an average diameter between 0.5 μm and 100 μm.

14. The depth filter layer according to claim 12 , wherein kieselguhr, perlite or the mixture thereof comprises particles with an average diameter between 0.5 μm and 100 μm.

15. The depth filter layer according to claim 11 , wherein the depth filter layer is produced from a mixture in which the content by weight of the at least one inorganic layer double hydroxide and the silicon dioxide and/or the at least one derivative thereof is 20-75%, the content by weight of the cellulose fibres and/or derivatives thereof is 30-80% and the content by weight of the organic wet strength agent is 0.5-10% and the contents by weight add up to 100%.

16. The depth filter layer according to claim 12 , wherein the depth filter layer is produced from a mixture in which the content by weight of the at least one inorganic layer double hydroxide and the kieselguhr or the perlite or the mixtures thereof is 20-75%, the content by weight of the cellulose fibres and/or derivatives thereof is 30-80% and the content by weight of the organic wet strength agent is 0.5-10% and the contents by weight add up to 100%.

17. A method for producing a depth filter layer, the method comprising the steps of:

(1) preparing cellulose fibres and/or derivatives thereof in at least one liquid medium;

(2) adding at least one inorganic layer double hydroxide;

(3) adding at least one organic wet strength agent to the mixture obtained in step (2);

(4) applying the suspension obtained in step (3) onto a carrier;

(5) removing the at least one liquid medium; and

(6) drying the depth filter layer obtained in step (5),

wherein the depth filter layer is produced from a mixture comprising a content by weight of the at least one inorganic layer double hydroxide of 10-65%, a content by weight of the cellulose fibres and/or derivatives thereof of 30-80% and a content by weight of the organic wet strength agent of 0.5-10%, based on the total weight of the mixture, and wherein the at least one organic wet strength agent reacts with carboxyl and/or OH groups of the cellulose fibres and/or derivatives thereof and the at least one inorganic layer double hydroxide to bridge components of the mixture to one another;

wherein the at least one inorganic layer double hydroxide comprises particles with an average diameter between 0.5 μm and 100 μm; and

wherein the depth filter layer is configured to bind nucleic acids adsorptively to the depth filter layer and to allow proteins to pass through the depth filter layer unimpeded.

18. The method according to claim 17 , wherein the at least one organic wet strength agent is added in step (2) and the at least one inorganic layer double hydroxide is added in step (3).

19. The method according to claim 17 , wherein the cellulose fibres and/or derivatives thereof are milled after step (1) and before step (2).

20. The method according to claim 17 , wherein the depth filter layer is dried at 100° C. to 250° C. in step (6).

21. The method according to claim 17 , wherein silicon dioxide and/or at least one derivative thereof is added as a further component before step (4).

22. The method according to claim 17 , wherein silicon dioxide and/or at least one derivative thereof is added together with the at least one inorganic layer double hydroxide in step (2).

23. The method according to claim 17 , wherein kieselguhr, perlite or a mixture thereof is added as further components before step (4).

24. The method according to claim 17 , wherein kieselguhr, perlite or a mixture thereof is added together with the at least one inorganic layer double hydroxide as further components in step (2).

25. A filtration device, containing at least the depth filter layer according to claim 1 .

26. A method for separating nucleic acids from proteins in a liquid medium by using at least the depth filter layer according to claim 1 , the method comprising the steps of:

(a) contacting the liquid medium which contains the nucleic acids and the proteins with the at least one depth filter layer;

(b) retaining the nucleic acids upon the at least one depth filter layer; and

(c) obtaining a filtrate containing the proteins and the liquid medium.

27. The method according to claim 26 , wherein the method further comprises the step of

(d) washing, after step (c), the depth filter layer with the liquid medium and/or with a rinsing medium in order to increase the content of the proteins in the filtrate.

28. The method according to claim 26 , wherein the proteins are selected from the group of the antibodies, hormones, enzymes, peptides or mixtures thereof.