Composite carbon fibers
View Patent ↗An object of the present invention is to provide composite carbon fibers in which multiwalled carbon nanotubes are homogeneously dispersed between graphitized carbon nanofibers and near the surface of the graphitized carbon nanofibers, the composite carbon fibers being capable of easily being dispersed in a matrix such as resin without leaving aggregates, and also imparting low resistance. Disclosed are composite carbon fibers comprising multiwalled carbon nanotubes having a fiber diameter of 5 nm or more and 30 nm or less and graphitized carbon nanofibers having a fiber diameter of 50 nm or more and 300 nm or less, wherein the multiwalled carbon nanotubes are homogeneously dispersed between the graphitized carbon nanofibers and near the surface of the graphitized carbon nanofibers.
1. Aggregates comprising composite carbon fibers, in which the composite carbon fibers comprise multiwalled carbon nanotubes having a fiber diameter of from 5 nm to 30 nm and an aspect ratio of from 100 to 1000 and graphitized carbon nanofibers having a fiber diameter of from 50 nm to 300 nm,
wherein the multiwalled carbon nanotubes are homogeneously dispersed between the graphitized carbon nanofibers and near the surface of the graphitized carbon nanofibers, and the dispersion state is a state where carbon nanofibers extend through the space between carbon nanotubes disentangled in a loose state.
2. The aggregates according to claim 1 , wherein a compressed specific resistance at a compressed density of 0.8 g/cm 3 measured using the composite carbon fibers is lower than a compressed specific resistance at a compressed density of 0.8 g/cm 3 measured using the multiwalled carbon nanotube alone, and is also lower than a compressed specific resistance at a compressed density of 0.8 g/cm 3 measured using the graphitized carbon nanofiber alone.
3. The aggregates according to claim 1 , wherein the multiwalled carbon nanotubes have C 0 value of from 0.680 nm to 0.690 nm, and the graphitized carbon nanofibers have C 0 value of from 0.676 nm to 0.680 nm.
4. The aggregates according to claim 1 , wherein the multiwalled carbon nanotubes have an oxidation initiation temperature of from 400° C. to 550° C. or lower, and the graphitized carbon nanofibers have an oxidation initiation temperature of from 600° C. to 700° C.
5. The aggregates according to claim 1 , wherein the amount of the multiwalled carbon nanotubes is from 1% by mass to 50% by mass in the composite carbon fibers.
6. The aggregates according to claim 1 , in which the composite carbon fibers do not substantially contain multiwalled carbon nanotube aggregates having an aggregate size of 1 μm or more.
7. The aggregates according to claim 1 , wherein a ratio (p/p 0 ) of a density p of the composite carbon fibers when compressed under a load of 1,000 N or more to a density p 0 of graphitized carbon nanofibers when compressed under the same load is 0.95 or more.
8. The aggregates according to claim 1 , wherein 50% particle diameter (D 50 ) in volume-based cumulative particle size distribution by laser diffraction particle size analysis is from 5 μm to 20 μm.
9. The aggregates according to claim 1 , wherein a weight ratio of the graphitized carbon nanofibers to the multiwalled carbon nanotubes is from 80/20 to 98/2.
10. An electrode for a battery, comprising the aggregates according to claim 1 .
11. A method for producing aggregates, the method comprising:
mixing multiwalled carbon nanotubes and graphitized carbon nanofibers in water to obtain a slurry, the carbon nanotubes having a fiber diameter of from 5 nm to 30 nm and an aspect ratio of from 100 to 1000, and the graphitized carbon nanofibers having a fiber diameter of from 50 to 300 nm;
passing the slurry through a pulverizing nozzle equipped in a high pressure dispersion device;
drying the slurry passing from the pulverizing nozzle; and
pulverizing the dried product,
wherein, in the pulverized dried product, the multiwalled carbon nanotubes are homogeneously dispersed between the graphitized carbon nanofibers and near the surface of the graphitized carbon nanofibers, and the dispersion state is a state where carbon nanofibers extend through the space between carbon nanotubes disentangled in a loose state.