Electrode material for aluminum electrolytic capacitor, and process for producing same
The present invention provides an electrode material for an aluminum electrolytic capacitor, which does not require any etching treatment and which has improved bending strength. Specifically, the present invention provides an electrode material for an aluminum electrolytic capacitor, which comprises, as constituent elements, a sintered body of a powder of at least one member selected from the group consisting of aluminum and aluminum alloys and an aluminum foil substrate that supports the sintered body thereon, which is characterized in that (1) the powder has an average particle size D 50 of 0.5 to 100 μm, (2) the sintered body is formed on one surface or both surfaces of the aluminum foil substrate and has a total thickness of 20 to 1,000 μm, and (3) the aluminum foil substrate has a thickness of 10 to 200 μm and an Si content of 10 to 3,000 ppm.
1. An electrode material for an aluminum electrolytic capacitor, comprising, as constituent elements, a sintered body of a powder of at least one member selected from the group consisting of aluminum and aluminum alloys, and an aluminum foil substrate supporting the sintered body thereon, wherein
(1) the powder has an average particle size D 50 of 0.5 to 100 μm and an Si content of less than 100 ppm,
(2) the sintered body is formed on one surface or both surfaces of the aluminum foil substrate, and the sintered body or sintered bodies have a total thickness of 20 to 1,000 μm, and
(3) the aluminum foil substrate has a thickness of 10 to 200 μm and an Si content of 10 to 3,000 ppm.
2. A method for producing an electrode material for an aluminum electrolytic capacitor, comprising the steps of:
Step 1: forming a film made from a composition comprising a powder of at least one member selected from the group consisting of aluminum and aluminum alloys on an aluminum foil substrate; wherein
(1) the powder has an average particle size D 50 of 0.5 to 100 μm and an Si content of less than 100 ppm,
(2) the film is formed on one surface or both surfaces of the aluminum foil substrate, and the total thickness of the film or films is 20 to 1,000 μm,
(3) the aluminum foil substrate has a thickness of 10 to 200 μm and an Si content of 10 to 3,000 ppm:
Step 2: sintering the film, after Step 1, at a temperature in the range of 560 to 660° C., the method being free from an etching treatment.
3. The production method according to claim 2 , which further comprises Step (3): anodizing the sintered film.