Thermoplastic poly-ether-ester elastomer resin composition and elastic monofilaments prepared therefrom
The present invention relates to a poly-ether-ester elastomer resin composition and elastic monofilaments prepared therefrom, and more specifically to a thermoplastic poly-ether-ester elastomer resin composition and elastic monofilaments prepared therefrom, wherein the thermoplastic poly-ether-ester elastomer resin composition is prepared from a poly-ether-ester block copolymer, a heat stabilizer, a UV absorber, a hindered amine light stabilizer, and porous silica, thereby ensuring excellent perceived quality, spinnability and weavability.
1. A poly-ether-ester elastomer resin composition, comprising: 100 parts by weight of a poly-ether-ester block copolymer; 0.05-2.0 parts by weight of a heat stabilizer; 0.1-2.0 parts by weight of an ultraviolet absorber; 0.1-1.0 parts by weight of a hindered amine light stabilizer; and 0.05-1.0 parts by weight of porous silica,
wherein the porous silica is synthetic porous silica including an ingredient for capturing total volatile organic compounds and has the following Formula 1:
Al 2 Si 2 O 5 (OH) x .M y Formula 1
wherein M is a metal selected from among P, Ca, Zn, Fe, K, Mn, Mo, Ag, Mg and Ti,
x is an integer of 1 -5, and
y is an integer of 2 -7.
2. The poly-ether-ester elastomer resin composition of claim 1 , wherein the heat stabilizer is one or a mixture of two or more selected from the group consisting of 2,2′-m-phenylene bis(2-oxazoline), 4,4′-bis(alpha, alpha-dimethylbenzyl diphenylamine), and N,N′-hexane-1,6-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl propionamide)).
3. The poly-ether-ester elastomer resin composition of claim 1 , wherein the ultraviolet absorber is one or a mixture of two or more selected from the group consisting of 2-(2H-benzotriazloe-2-yl)-4-6-bis(1-methyl-1-phenylethyl)phenol, 2-(5-chloro(2H)-benzotriazloe-2-yl)-4-methyl-6-(tert-butyl)phenol, 2-(4,6-diphenyl-1,3,5-triazin-2-yl)-5-(hexyloxy)-phenol, and 2,4-di-tert-butyl phenyl-3,5-di-tert-butyl-4-hydroxy benzoate.
4. The poly-ether-ester elastomer resin composition of claim 1 , wherein the hindered amine light stabilizer is selected from the group consisting of a polycondensation product of dibutylamine-1,3,5-triazine-N,N-bis(2,2,6,6-tetramethyl)-4-piperidyl-1,6-hexamethylenediamine and N-(2,2,6,6-tetramethyl-4-piperidyl)butylamine, poly-6-(1,1,3,3-tetramethylbutyl)amino-s-triazine-2,4-diyl-(2,2,6,6-tetramethyl-4-piperidylimino-hexamethylene-(2,2,6,6-tetramethyl-4-piperidyl)imino, and a mixture thereof.
5. The poly-ether-ester elastomer resin composition of claim 1 , wherein a total amount of volatile organic compounds, measured by MS300-55, is 20 ppm or less.
6. An elastic monofilament prepared using the poly-ether-ester elastomer resin composition of claim 1 .
7. An elastic fabric comprising the elastic monofilament of claim 6 .
8. An elastic monofilament prepared using the poly-ether-ester elastomer resin composition of claim 2 .
9. An elastic monofilament prepared using the poly-ether-ester elastomer resin composition of claim 3 .
10. An elastic monofilament prepared using the poly-ether-ester elastomer resin composition of claim 4 .
11. An elastic monofilament prepared using the poly-ether-ester elastomer resin composition of claim 5 .
12. An elastic fabric comprising the elastic monofilament of claim 8 .
13. An elastic fabric comprising the elastic monofilament of claim 9 .
14. An elastic fabric comprising the elastic monofilament of claim 10 .
15. An elastic fabric comprising the elastic monofilament of claim 11 .