Coated paper having a coating structure with controlled distribution of latex and method for preparing the same
Disclosed is coated paper having a coating structure in which styrene-butadiene latex distribution of a paper coating layer is controlled in order to reduce fold cracking of the coated paper and a method for manufacturing the same. The coated paper in which different types of latexes are separately applied to two coating layers exhibits considerably improved stiffness and reduced fold crack, as compared to the existing coated paper.
1. A method for preparing coated paper comprising:
preparing a first coating solution comprising a latex having a particle size of 70 to 120 nm and a glass transition temperature of 10 to 30° C. and a second coating solution comprising a latex having a particle size of 120 to 200 nm and a glass transition temperature of −30 to 0° C.;
coating a base paper with the first coating solution, followed by drying, to form a first coating layer as a pre-coating layer; and
coating the first coating layer with the second coating solution, followed by drying, to form a second coating layer as a top coating layer,
wherein a total thickness of the coating layers of the first coating layer and the second coating layer is within the range of 20 to 60 μm.
2. The method according to claim 1 , wherein the first coating solution or the second coating solution is prepared by mixing 5 to 20 parts by weight of a styrene-butadiene latex and 0.1 to 9 parts by weight of a thickener, with respect to 100 parts by weight of the pigment and the auxiliary pigment, to have a solid content of 60 to 75% and pH of 8 to 11.
3. The method according to claim 1 , wherein the base paper is a base paper for art paper, a base paper for art board paper, or a base paper for cardboard, each having a basis weight of 70 to 350 g/M 2 .
4. The method according to claim 1 , wherein the coating layer is formed using a super calendar or a soft-nip calendar.