Ni-Cr-Co-based alloy having high-temperature corrosion resistance, and poppet valve surface-modified with the same
There is provided a surface-coating material having excellent cracking resistance and peeling resistance, and having excellent high-temperature corrosion resistance properties; and a poppet valve coated with the surface-coating material. The Ni—Cr—Co-based alloy comprises 40.0 to 50.0 mass % of Cr, 10.0 to 20.0 mass % of Co, 0.5 to 5.0 mass % of Nb, 0.01 to 5.0 mass % of Fe and 0.1 to 3.0 mass % of Si, with the remainder being 26.0 to 40.0 mass % of Ni and unavoidable impurities. The Ni—Cr—Co-based alloy may additionally comprise one or more elements selected from Mo, W, Mn, Ti, Al, B and C in a total amount of 5.0 mass % or less. The content of each of Ti and Al is 3.0 mass % or less and the content of each of B and C is 1.0 mass % or less. In the poppet valve, at least a face portion is coated with the Ni—Cr—Co-based alloy.
1. A poppet valve, which is subjected to surface modification through any application process selected from spraying, overlaying, and vapor deposition, using a Ni—Cr—Co-based alloy having high-temperature corrosion resistance and having a composition of:
40.0 to 50.0 mass % of Cr;
10.0 to 20.0 mass % of Co;
0.5 to 5.0 mass % of Nb;
0.01 to 5.0 mass % of Fe;
0.1 to 3.0 mass % of Si; and
the remainder being 26.0 to 40.0 mass % of Ni and unavoidable impurities.
2. The poppet valve according to claim 1 , wherein the surface modification is applied to at least a face portion.
3. A poppet valve, which is subjected to surface modification through any application process selected from spraying, overlaying, and vapor deposition, using a Ni—Cr—Co-based alloy having high-temperature corrosion resistance and having a composition of:
40.0 to 50.0 mass % of Cr;
10.0 to 20.0 mass % of Co;
0.5 to 5.0 mass % of Nb;
0.01 to 5.0 mass % of Fe;
0.1 to 3.0 mass % of Si;
one or more elements selected from Mo, W, Mn, Ti, Al and B in a total amount of 5.0 mass % or less, the content of each of Ti and Al being 3.0 mass % or less, and the content of B being 1.0 mass % or less; and
the remainder being 26.0 to 40.0 mass % of Ni and unavoidable impurities.
4. The poppet valve according to claim 3 , wherein the surface modification is applied to at least a face portion.