Urea passivation technique and new product passivated urea, to make urea or urea-based compound universally blendable
The invention concerns a method of producing passivated urea or urea based compounds for fertilizer blends wherein the urea particles are treated with a mineral acid that reacts with urea and creates a grasping layer. Thereafter a solid base in powder form is added in excess to the particles to coat the acidified particle surface. The invention also concerns a fertilizer blend comprising the passivated urea or urea based compounds with one or more of AN or AN-based compound, NS products, superphosphates, and more generally with a priori most compounds that urea is susceptible to react with when in direct contact. A safe blend comprises more than 40 weight % of the passivated urea.
1. A method of producing passivated particles comprising urea, or urea-based compounds, for fertilizer blends, said method comprising:
treating urea containing particles with 0.1 to 2.0 weight % of a mineral acid that reacts with urea, so as to create an acidified particle surface and form a grasping layer made of a double salt of urea; and thereafter
adding an excess, 2 to 6 weight %, based on the weight of the urea-containing particles, of a solid base in powder form to the particles so as to coat the acidified particle surface and obtain a layer comprising 1) said grasping layer, 2) metal salts formed from reacting said mineral acid with said solid base in powder form, and 3) unreacted base.
2. The method according to claim 1 , wherein the urea-containing particles are treated with 0.9 to 1.0 weight % acid and 2.5 to 4.0 weight % solid base, based on the weight of the urea-containing particles.
3. The method according to claim 1 , wherein the urea-containing particles are treated with 0.2 to 0.8 weight % acid and 3-5.8 weight % base, based on the weight of the urea-containing particles.
4. The method according to claim 1 , wherein a further acid treatment step is performed.
5. The method according to claim 1 , wherein the mineral acid is sulphuric acid, phosphoric acid or nitric acid.
6. The method according to claim 1 , wherein the solid base is MgO, dolomite, magnesite, calcite, calcium oxide or calcium hydroxide limestone, or chalk.
7. The method according to claim 1 , wherein the urea based compound of the urea-containing particles is urea, UAS, NPK, NK, NP, urea with micronutrients, or any mixture thereof.
8. The method according to claim 1 , wherein the urea-containing particles are pretreated by drying or preheating.
9. The method according to claim 1 , wherein the passivated urea-containing particles are further coated.
10. A fertilizer blend comprising:
passivated particles comprising urea, or a urea-based compound, produced by the method according to claim 1 , and
one or more of ammonium nitrate, an ammonium nitrate-based compound, calcium nitrate, superphosphates, NS products, or a compound which urea is susceptible to react with when in direct contact.
11. The fertilizer blend according to claim 10 , comprising passivated particles comprising urea, or a urea-based compound, and ammonium nitrate-based compounds, and optionally salts able to bind crystallization water.
12. The fertilizer blend according to claim 11 , wherein the salt is magnesium nitrate, magnesium sulphate or a mixture thereof.
13. The fertilizer blend according to claim 11 , wherein the amount of salt is 0.5 to 3 weight %.
14. The fertilizer blend according to claim 11 , comprising passivated particles comprising urea, or a urea-based compound, and ammonium nitrate comprising magnesium nitrate.
15. The fertilizer blend according to claim 10 , comprising more than 40 weight % of passivated particles comprising urea, or urea-based compound.
16. Passivated particles of urea or urea-based compounds, having a surface comprising 1) a grasping layer of double salts of urea, 2) metal salts and 3) unreacted base,
wherein the passivated particles of urea or urea-based compounds are obtained by treating urea-containing particles with 0.1 to 2.0 weight % of a mineral acid that reacts with urea, and an excess, 2 to 6 weight %, of a solid base in powder form, based on the weight of the urea-containing particles.