Chloroprene rubber composition, and vulcanizate and molding thereof
To provide a chloroprene rubber composition providing good permanent compression set and excellent mechanical strength, a vulcanizate of the composition, and a molded article of the composition. A chloroprene rubber composition including a chloroprene rubber and a natural rubber in a total amount of 100 parts by mass, a copolymer of styrene and butadiene in an amount of 0.1 to 10 parts by mass, ethylene thiourea in an amount of 0.1 to 3.0 parts by mass, and dipentamethylenethiuram tetrasulfide in an amount of 0.1 to 3.0 parts by mass is vulcanized after or during molding of the composition to yield a vulcanized molding.
1. A chloroprene rubber composition comprising:
a chloroprene rubber and a natural rubber in a total amount of 100 parts by mass;
a block copolymer of styrene and butadiene in an amount of 0.1 to 10 parts by mass;
ethylene thiourea in an amount of 0.1 to 3.0 parts by mass; and
dipentamethylenethiuram tetrasulfide in an amount of 0.1 to 3.0 parts by mass,
wherein the blending ratio of the chloroprene rubber and the natural rubber (chloroprene rubber/natural rubber) is 60/40 to 95/5 by mass ratio.
2. The chloroprene rubber composition according to claim 1 , wherein the chloroprene rubber includes a 2,3-dichiorobutadiene unit in an amount of 5 to 20% by mass.
3. A vulcanizate obtained by vulcanization of the chloroprene rubber composition according to claim 1 .
4. A molding obtained by vulcanization of the chloroprene rubber composition according to claim 1 after or during molding of the composition.
5. The molding according to claim 4 , wherein the molding is a wiper blade or a vibration isolator.
6. The chloroprene rubber composition according to claim 1 , wherein the block copolymer of styrene and butadiene includes styrene and butadiene in a mass ratio (styrene/butadiene) of 25/75 to 45/55.
7. A vulcanizate obtained by vulcanization of the chloroprene rubber composition according to claim 6 .
8. A molding obtained by vulcanization of the chloroprene rubber composition according to claim 6 after or during molding of the composition.
9. The molding according to claim 8 , wherein the molding is a wiper blade or a vibration isolator.
10. The chloroprene rubber composition according to claim 1 , wherein the blending ratio of the chloroprene rubber and the natural rubber (chloroprene rubber/natural rubber) is 60/40 by mass ratio.
11. The chloroprene rubber composition according to claim 1 , wherein the blending ratio of the chloroprene rubber and the natural rubber (chloroprene rubber/natural rubber) is 95/5 by mass ratio.