Adhesive composition that can be peeled after crosslinking

1. An adhesive composition comprising:

(i) from 58 to 80% by weight of a moisture-crosslinkable polymer (A) comprising at least:

as main chain, a polyurethane (A2) having a number-average molecular weight between 600 Da and 60 kDa, being the condensation product of a polyether polyol and/or a polyester polyol with polyisocyanates, and

an alkoxysilane terminal radical of formula (I),

—Si(R 1 ) p (OR 2 ) 3-p   (I)

in which:

R 1 and R 2 , which are identical or different, each represent a linear or branched alkyl radical having 1 to 4 carbon atoms, and when there are multiple R 1 radicals, the R 1 radicals may be identical or different, and when there are multiple R 2 radicals, the R 2 radicals may be identical or different;

p is an integer equal to 0, 1 or 2;

said alkoxysilane radicals being connected to the main chain directly by its available bond or indirectly

(ii) from 8 to 20% by weight of a silica (B) having a BET specific surface area between 150 and 250 m 2 /g;

(iii) from 4 to 15% by weight of an oligomer of a vinyl derivative of an alkoxyalkylsilane (C) having a number-average molecular weight between 500 Da and 5 kDa,

(iv) from 0.01 to 3% by weight of a crosslinking catalyst (D), and

(v) from 0.1 to 5% by weight of rubber granulates of non-spherical shape having a size between 0.5 and 2 mm.

2. The adhesive composition according to claim 1 , wherein the composition comprises from 60 to 77% of polymer (A), from 10 to 18% of pyrogenic silica (B), from 5 to 12% of oligomer (C) and from 0.1 to 2% of catalyst (D).

3. The adhesive composition according to claim 1 , wherein the composition comprises, in addition, up to 3% of a hydrolysable alkoxysilane derivative, as a desiccant.

4. A method for fastening an article to a substrate included in the floors, vertical surfaces and/or ceilings of dwellings, comprising:

(a) depositing the adhesive composition as defined in claim 1 in the form of a bead having a diameter of 2 to 10 mm onto the surfaces of the article or of the substrate intended to be in contact;

(b) applying the article to the substrate by simple manual pressure; then

(c) crosslinking said adhesive composition under the effect of atmospheric moisture over a time between 1 hour and 48 hours.

5. The method according to claim 4 , wherein the substrate is included in a vertical surface, and the bead of adhesive composition is deposited on the planar surface of the article intended to be brought into contact with the substrate.

6. The method according to claim 5 , wherein the weight of the article to be fastened corresponds to a shear stress exerted on the joint constituted of the crosslinked adhesive composition, wherein the shear stress ranges from 3 to 20 kg/cm 2 .

7. The method according to claim 4 , wherein the article to be fastened can be used for the purposes of outfitting or decorating a dwelling.

8. The method according to claim 5 , wherein the bead of adhesive composition is placed on the upper half of the planar surface of the article intended to be in contact with the substrate, in the vicinity of the line of contact between said surface and the substrate.

9. A method for separating the article attached to a substrate in accordance with the method defined in claim 4 , comprising the implementation of an adhesive failure.

10. The adhesive composition according to claim 1 , wherein the size of the non-spherical shape rubber granulates is between 0.8 and 1.2 mm.

11. The method according to claim 4 , wherein the substrate is part of a floor, vertical surface or ceiling of a dwelling.

12. The method according to claim 4 , wherein the bead has a diameter from 4 to 10 mm.

13. The method according to claim 4 , wherein the crosslinking is over a time between 4 hours and 24 hours.

14. The adhesive composition according to claim 1 , wherein the oligomer is obtained by oligomerization of a vinyl derivative of an alkoxyalkylsilane.

15. The adhesive composition according to claim 1 , wherein the polymer (A) has the formula (II):

in which:

R 1 and R 2 , which are identical or different, each represent a linear or branched alkyl radical having 1 to 4 carbon atoms, and when there are multiple R 1 radicals, the R 1 radicals may be identical or different, and when there are multiple R 2 radicals, the R 2 radicals may be identical or different;

R 3 represents a hydrocarbon divalent radical comprising from 5 to 15 carbon atoms which may be aromatic or aliphatic, linear, branched or cyclic;

R 4 represents a linear or branched alkylene divalent radical comprising from 1 to 4 carbon atoms;

R 5 represents a linear alkylene divalent radical comprising from 1 to 3 carbon atoms;

n is an integer such that the number-average molecular weight of the polyether block of formula

[OR 4 ] n — is between 300 Da and 30 kDa;

m is an integer such that the number-average molecular weight of the polymer of formula (II) is between 600 Da and 60 kDa; and

p is an integer equal to 0, 1 or 2.