Method and apparatus for applying a mid-IR graded-index microstructure to an optical fiber tip to achieve anti-reflective properties

1. A method for preventing reflection losses in optical fibers, the method comprising:

heating an appropriately terminated chalcogenide glass optical fiber tip to form a heated optical fiber tip;

flattening the heated optical fiber tip to form a flattened optical fiber tip;

heating the flattened optical fiber tip; and

imprinting a microstructure onto the flattened optical fiber tip.

2. The method of claim 1 , wherein the chalcogenide glass optical fiber is selected from the group consisting of optical fibers comprised of As 2 S 3 glass, Ge 33 As 12 Se 33 glass, As x Se x glass, Ge x Sb x Se x glass, AS 40 S 60 glass, Te 25 As 40 Se 33 glass, and germanium sulfide glasses.

3. The method of claim 2 , wherein the chalcogenide glass is As 2 S 3 .

4. The method of claim 3 , further comprising applying pressure to the heated As 2 S 3 fiber tip against a substantially flat surface.

5. The method of claim 3 , further comprising applying pressure to the flattened As 2 S 3 fiber tip against a negative imprinting surface.

6. The method of claim 4 , further comprising causing the pressure applied to the heated As 2 S 3 fiber tip to be in the range of about 3,000 PSI to about 80,000 PSI.

7. The method of claim 5 , further comprising causing the pressure applied to the flattened As 2 S 3 fiber tip to be in the range of about 3,000 PSI to about 80,000 PSI.

8. The method of claim 4 , further comprising causing the heated As 2 S 3 fiber tip to be heated to a range of about 170° C. to about 270° C.

9. The method of claim 4 , further comprising causing the flattened As 2 S 3 fiber tip to be heated to a range of about 170° C. to about 270° C.

10. The method of claim 5 , further comprising causing the imprinting surface to have a plurality of protrusions and recesses.

11. A method for preventing reflection losses in properly terminated chalcogenide glass fibers, the method comprising:

securing a properly terminated chalcogenide glass fiber into a ferrule, so that a tip of the properly terminated chalcogenide glass fiber protrudes about 1 mm to 2 mm from the ferrule;

fastening the ferrule to a fixture;

lowering the fixture onto a heating surface, such that the heating surface transfers heat to the properly terminated chalcogenide glass fiber tip without touching the properly terminated chalcogenide glass fiber tip;

adjusting the orientation of the fixture with a hollow cylinder placed between the fixture and the heating surface to ensure perpendicularity of the properly terminated chalcogenide glass fiber tip relative to the heating surface;

lowering the fixture so that the properly terminated chalcogenide glass fiber tip contacts the heating surface;

replacing the heating surface with a hot imprinting surface;

lowering the fixture onto the hot imprinting surface, such that the hot imprinting surface transfers heat to the properly terminated chalcogenide glass fiber tip without touching the properly terminated chalcogenide glass fiber tip; and

lowering the fixture so that the properly terminated chalcogenide glass fiber tip contacts the hot imprinting surface.

12. The method of claim 11 , wherein the chalcogenide glass optical fiber is selected from the group consisting of optical fibers comprised of As 2 S 3 glass, Ge 33 As 12 Se 33 glass, As x Se x glass, Ge x Sb x Se x glass, AS 40 S 60 glass, Te 25 As 40 Se 33 glass, and germanium sulfide glasses.

13. The method of claim 12 , wherein the chalcogenide glass is As 2 S 3 glass.

14. The method of claim 13 , further comprising applying a pressure of about 3,000 PSI to about 144,000 PSI to the properly terminated As 2 S 3 fiber tip against the heating surface.

15. The method of claim 14 , further comprising applying a pressure of about 3,000 PSI to about 144,000 PSI to the properly terminated As 2 S 3 fiber tip against the hot imprinting surface.

16. The method of claim 15 , further comprising removing the properly terminated As 2 S 3 fiber tip from heating surface after a contact period of about 10 seconds to about 300 seconds.

17. The method of claim 15 , further comprising removing properly terminated As 2 S 3 fiber tip from the hot imprinting surface after a contact period of about 10 seconds to about 300 seconds.

18. The method of claim 15 , wherein the step of lowering the fixture onto a heating surface includes lowering the properly terminated As 2 S 3 fiber tip to within about 100 μm to about 200 μm of the heating surface.

19. The method of claim 15 , wherein the step of lowering the fixture onto the hot imprinting surface includes lowering the properly terminated As 2 S 3 fiber tip to within about 100 μm to about 200 μm of the hot imprinting surface.