Encapsulating material for solar cell and solar cell module
An encapsulating material for solar cell that is capable of suppressing the corrosion of metal and the occurrence of yellowing at a high temperature and has excellent long-term reliability in a constant temperature and humidity is provided. The encapsulating material for solar cell of the invention contains an ethylene/α-olefin copolymer, a hindered amine-based light stabilizer, a hindered phenol-based stabilizer, and a phosphorous-based stabilizer as essential components.
1. A solar cell module comprising:
a transparent surface protective member;
a back surface protective member;
a solar cell element; and
an encapsulating layer which is formed by crosslinking an encapsulating material for solar cell and encapsulates the solar cell element between the transparent surface protective member and the back surface protective member,
wherein the encapsulating material for solar cell comprises an ethylene/α-olefin copolymer, a hindered amine-based light stabilizer, a hindered phenol-based stabilizer, and a phosphorous-based stabilizer,
a content of the hindered phenol-based stabilizer in the encapsulating material for solar cell is in a range of 0.01 parts by weight to 0.06 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer,
a content of the phosphorous-based stabilizer in the encapsulating material for solar cell is in a range of 0.02 parts by weight to 0.2 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer,
wherein the hindered phenol-based stabilizer includes octadecyl-3-(3,5-di-t-butyl-4-hydroxphenyl)propionic acid ester, and the phosphorous-based stabilizer includes tris(2,4-di-tert-butylphenyl)phosphite.
2. The solar cell module according to claim 1 ,
wherein a content of the hindered amine-based light stabilizer in the encapsulating material for solar cell is in a range of 0.01 parts by weight to 2.0 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer.
3. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell further comprises an organic peroxide.
4. The solar cell module according to claim 3 ,
wherein a one-minute half-life temperature of the organic peroxide is in a range of 100° C. to 170° C., and
a content of the organic peroxide in the encapsulating material for solar cell is in a range of 0.1 parts by weight to 3 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer.
5. The solar cell module according to claim 1 ,
wherein the ethylene/α-olefin copolymer satisfies the following requirements a1) to a4):
a1) a content ratio of a structural unit derived from ethylene is in a range of 80 mol % to 90 mol %, and a content ratio of a structural unit derived from an α-olefin having 3 to 20 carbon atoms is in a range of 10 mol % to 20 mol %;
a2) MFR, which is based on ASTM D1238 and measured under conditions of a temperature of 190° C. and a load of 2.16 kg, is in a range of 10 g/10 minutes to 50 g/10 minutes;
a3) a density, which is measured on the basis of ASTM D1505, is in a range of 0.865 g/cm 3 to 0.884 g/cm 3 ; and
a4) a shore A hardness, which is measured on the basis of ASTM D2240, is in a range of 60 to 85.
6. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell further comprises a silane coupling agent, and
a content of the silane coupling agent in the encapsulating material for solar cell is in a range of 0.1 parts by weight to 5 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer.
7. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell further comprises an ultraviolet absorber, and
a content of the ultraviolet absorber in the encapsulating material for solar cell is in a range of 0.005 parts by weight to 5 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer.
8. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell further comprises a crosslinking aid, and
a content of the crosslinking aid in the encapsulating material for solar cell is in a range of 0.05 parts by weight to 5 parts by weight with respect to 100 parts by weight of the ethylene/α-olefin copolymer.
9. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell is obtained by melting and kneading the ethylene/α-olefin copolymer, the hindered amine-based light stabilizer, the hindered phenol-based stabilizer, and the phosphorous-based stabilizer, and then molding by extrusion the mixture into a sheet shape.
10. The solar cell module according to claim 1 ,
wherein the encapsulating material for solar cell has a sheet shape.
11. The solar cell module according to claim 1 ,
wherein the hindered amine-based light stabilizer includes bis(2,2,6,6-tetramethyl-4-piperidyl)sebacate.