Dust prevention compositions, coatings and processes of making
Compositions, applications, coatings, processes of making and applying compositions and compositions for preventing dust buildup on plastic and wood surfaces such as on ceiling fan blades, portable fan blades, stand fan blades, window blinds, appliances, furniture, cabinet knobs, and drawer pulls. The compositions and coating prevent dust buildup by (1) dissipating static charges on the blades and (2) creating a very smooth blade surface that prevents dust particles getting “captured”. The coating can have a clear matte finish and contains an anti-static and high lubricity additive to deter the accumulation of dust. After applying the coating the dry time of the coatings by thin coat gravure rollers is approximately four minutes. When applied the coating can result in up to approximately 50% less dust buildup over a one week period of time.
1. The dust prevention composition, wherein the composition comprises:
a thermoset adhesion;
an anti-static matting agent;
a lubricity agent;
conductivity component;
a dispersant;
a UV(ultra violet) activator;
a solvent; and
a binder, wherein the composition is useful as a coating on a surface to reduce dust buildup on the surface over time.
2. The dust prevention composition of claim 1 , wherein the composition further includes:
acrylic resin as the thermoset adhesion;
fumed alumina as the anti-static matting agent;
PDMS(Polydimethylsiloxane) as the lubricity agent;
alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
hydrophobic copolymer polyelectrolyte as the dispersant,
2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
Ethanol and Isopropyl Alcohol as the solvent; and
polyamide resin as the binder.
3. The dust prevention composition of claim 2 , wherein the composition further includes:
approximately 2.08% to approximately 5.00% acrylic resin as the thermoset adhesion;
approximately 1.67% to approximately 4.00% fumed alumina as the anti-static matting agent;
approximately 1.25% to approximately 3.00% PDMS (Polydimethylsiloxane) as the lubricity agent;
approximately 0.83% to approximately 2.00% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.22% to approximately 0.50% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.02% to approximately 0.05% 2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 80% to approximately 51.90% Ethanol and Isopropyl Alcohol as the solvent; and
approximately 13.93% to approximately 33.55% polyamide resin as the binder.
4. The dust prevention composition of claim 3 , wherein the composition further includes:
approximately 3.12% to approximately 4.17% acrylic resin as the thermoset adhesion;
approximately 2.50% to approximately 3.34% fumed alumina as the anti-static matting agent;
approximately 1.87% to approximately 2.50% PDMS (Polydimethylsiloxane) as the lubricity agent;
approximately 1.25% to approximately 1.67% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.31% to approximately 0.42% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.03% to approximately 0.04% 2,5-thiophenediylbis (5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 60% to approximately 70% Ethanol; and Isopropyl Alcohol as the solvent; and
approximately 13.93% to approximately 33.55% polyamide resin as the binder.
5. The dust prevention composition of claim 4 , wherein the composition includes approximately 51.9% Ethanol and includes:
approximately 5.00% acrylic resin as the thermoset adhesion;
approximately 4.00% fumed alumina as the anti-static matting agent;
approximately 3.00% PDMS(Polydimethylsiloxane) as the lubricity agent;
approximately 2.00% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.50% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.05% 2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 51.90% Ethanol; and Isopropyl Alcohol as the solvent; and
approximately 33.55% polyamide resin as the binder.
6. The dust prevention composition of claim 4 , wherein the composition includes approximately 60% Ethanol and includes:
approximately 4.17% acrylic resin as the thermoset adhesion;
approximately 3.34% fumed alumina as the anti-static matting agent;
approximately 2.50% PDMS(Polydimethylsiloxane) as the lubricity agent;
approximately 1.67% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.42% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.04% 2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 60% Ethanol; and approximately 5% Isopropyl Alcohol as the solvent; and
approximately 27.86% polyamide resin as the binder.
7. The dust prevention composition of claim 4 , wherein the composition includes approximately 70% Ethanol and includes:
approximately 3.12% acrylic resin as the thermoset adhesion;
approximately 2.50% fumed alumina as the anti-static matting agent;
approximately 1.87% PDMS(Polydimethylsiloxane) as the lubricity agent;
approximately 1.25% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.31% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.03% 2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 70% Ethanol and Isopropyl Alcohol as the solvent; and
approximately 20.92% polyamide resin as the binder.
8. The dust prevention composition of claim 4 , wherein the composition includes approximately 80% Ethanol and includes:
approximately 2.08% acrylic resin as the thermoset adhesion;
approximately 1.67% fumed alumina as the anti-static matting agent;
approximately 1.25% PDMS(Polydimethylsiloxane) as the lubricity agent;
approximately 0.83% alkylolammonium salt of an unsaturated acidic carboxylic acid ester as the conductivity component;
approximately 0.22% hydrophobic copolymer polyelectrolyte as the dispersant;
approximately 0.02% 2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole) as the UV(ultra violet) activator;
approximately 80% Ethanol; and Isopropyl Alcohol as the solvent; and
approximately 13.93% polyamide resin as the binder.
9. A dust prevention coating, comprising:
acrylic resin;
fumed alumina;
PDMS(Polydimethylsiloxane);
alkylolammonium salt of an unsaturated acidic carboxylic acid ester;
hydrophobic copolymer polyelectrolyte,
2,5-thiophenediylbis(5-tert-butyl-1,3-benzoxazole);
Ethanol and Isopropyl Alcohol; and
polyamide resin, wherein the coating is useful for preventing dust buildup on a surface.