Low dielectric constant glass fiber
A low dielectric constant glass fiber, in mass percentage, includes 50%˜60% of SiO 2 , 10%˜20% of Al 2 O 3 , 12%˜20% of B 2 O 3 , 0˜4% of CaO, 4%˜10% of MgO, 0.1%˜0.5% of Na 2 O+K 2 O, 0˜0.5% of Li 2 O, 0.2%˜3% of F 2 and 0˜0.2% of Fe 2 O 3 . Compared with the related art, the glass composition contains higher content of SiO 2 , which can greatly reduce dielectric properties of the glass fiber. Meanwhile, a small amount of F 2 is added thereto, which not only can effectively improve the fiberizing temperature of the glass fiber but also can reduce glass viscosity and density and reduce glass refractive index and dielectric properties. In addition, lower content of CaO is further contained, but almost no alkali metal particles such as Na 2 O+K 2 O are contained, which further reduces the dielectric properties of the glass fiber.
1. A glass fiber, in mass, comprising:
SiO 2
50%-60%;
Al 2 O 3
16.3%-18.3%;
B 2 O 3
17.2%-19.6%;
CaO
2%-4%;
MgO
4%-10%;
Na 2 O + K 2 O
0.1%-0.5%;
Li 2 O
0-0.5%;
F 2
0.2%-3%; and
Fe 2 O 3
0.01%-0.15%.
2. The glass fiber according to claim 1 , wherein the mass percentage of Li 2 O is 0.05%-0.2%.
3. The glass fiber according to claim 1 , in mass percentage, comprising:
SiO 2
52%-58%;
Al 2 O 3
16.3%-18.3%;
B 2 O 3
17.2%-19.6%;
CaO
2%-4%;
MgO
4%-6%;
Na 2 O + K 2 O
0.1%-0.3%;
Li 2 O
0.05%-0.2%;
F 2
0.5%-1.5%; and
Fe 2 O 3
0.01%-0.15%.
4. The glass fiber according to claim 1 , in mass percentage, comprising:
SiO 2
53%-56%;
Al 2 O 3
16.3%-18.3%;
B 2 O 3
17.2%-19.6%;
CaO
2%-3.5%;
MgO
4%-6%;
Na 2 O + K 2 O
0.15%-0.3%;
Li 2 O
0.15%-0.2%;
F 2
0.5%-1.5%; and
Fe 2 O 3
0.05%-0.15%.