Nonaqueous electrolyte secondary battery
A nonaqueous electrolyte secondary battery 100 according to this invention includes a positive electrode 10 , a negative electrode 20 , a separator 40 interposed between the positive electrode 10 and the negative electrode 20 , and a nonaqueous electrolyte solution. A porous heat-resistant layer 42 is additionally provided between the separator 40 and at least one electrode from among the positive electrode 10 and the negative electrode 20 . The porous heat-resistant layer 42 includes hollow particles 44 made of an inorganic material, and a binder 46.
1. A nonaqueous electrolyte secondary battery comprising a positive electrode, a negative electrode, a separator interposed between the positive electrode and the negative electrode, and a nonaqueous electrolyte solution,
the nonaqueous electrolyte secondary battery further comprising a porous heat-resistant layer that is disposed between the separator and at least one electrode from among the positive electrode and the negative electrode, and that is formed on a surface of the separator,
wherein the porous heat-resistant layer includes hollow particles consisting of an inorganic material and also includes a binder, and
the hollow particles have an average particle diameter of at least 0.50 μm and not more than 0.98 μm; and
wherein the hollow particles have a hollowness of from 3% to 30%, where the hollowness of a hollow particle is the ratio of the volume of the hollow portion of the hollow particle to the volume of the hollow particle and is determined by observing a particle cross-section with a scanning electron microscope (SEM), measuring from this cross-sectional SEM image the cross-sectional surface area of the overall particle and the cross-sectional surface area of the hollow portion alone, then carrying out a calculation according to the following formula (1)
Hollowness(%)=( r 3 /R 3 )×100 (1)
where R is the radius of an ideal circle having the same surface area as the cross-sectional surface area of the overall particle being measured, and r is the radius of an ideal circle having the same surface area as the cross-sectional surface area of the hollow portion alone.
2. The nonaqueous electrolyte secondary battery according to claim 1 , wherein the porous heat-resistant layer has a porosity of at least 45%, and
wherein the porosity of the porous heat-resistant layer is determined from the formula:
(1− W 1 ρ 1 V 1 )×100
where V 1 is the apparent volume of the porous heat-resistant layer, W 1 is the mass of the layer, and ρ 1 is the true density of the porous heat-resistant layer.
3. The nonaqueous electrolyte secondary battery according to claim 1 , wherein the hollow particles are formed of at least one type of inorganic compound selected from the group consisting of alumina, magnesia, zirconia, silica, boehmite and titania.
4. The nonaqueous electrolyte secondary battery according to claim 1 , wherein the hollow particles are produced by a method comprising:
mixing resin particles into a solution containing an inorganic starting material;
inducing the inorganic starting material to deposit around the resin particles to form a deposited material; and
firing the deposited material.