Drive belt
A power transmission belt is used by being wound around a flat pulley so that an outer peripheral surface thereof contacts with the flat pulley. A portion forming the outer peripheral surface is made of a rubber composition including an ethylene-α-olefin elastomer as a rubber component thereof. The dynamic viscoelasticity properties of the rubber composition in a belt length direction satisfy ((a loss tangent tan δ at a temperature of 25° C. and a dynamic strain of 3.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain 3.0%))×1000≦3.0 MPa −1 , and (a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 1.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 3.0%)≦1.30.
1. A power transmission belt used by being wound around a flat pulley so that an outer peripheral surface of the belt contacts with the flat pulley, comprising:
(a) a portion forming the outer peripheral surface made of a rubber composition;
(b) an adhesive rubber layer;
(c) a cord embedded in the adhesive rubber layer; and
(d) an inner peripheral rubber layer attached to the portion (a) through the adhesive layer;
wherein the rubber composition comprises:
100 parts by mass of ethylene-propylene-diene terpolymer as a rubber component,
30 to 70 parts by mass of an unsaturated metal carboxylate salt,
5 to 25 parts by mass of carbon black, and
an organic peroxide as a crosslinker;
wherein the ethylene-propylene-diene terpolymers has a Mooney viscosity ML 1+4 (100° C.) of 30 or more, and an ethylene content of 55 mass % or more;
wherein a total of 35 to 95 parts by mass of the unsaturated metal carboxylate salt and the carbon black are added relative to 100 parts by mass of the rubber component, and an mass ratio of the unsaturated metal carboxylate salt to the carbon black (unsaturated metal carboxylate salt/carbon black) is 1.2/1 to 14/1;
wherein dynamic viscoelasticity properties of the crosslinked rubber composition in a belt length direction satisfy:
((a loss tangent tan δ at a temperature of 25° C. and a dynamic strain of 3.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain 3.0%))×1000<3.0 MPa −1 , and (a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 1.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 3.0%)<1.30.
2. The power transmission belt of claim 1 , wherein the unsaturated metal carboxylate salt includes zinc dimethacrylate.
3. The power transmission belt of claim 1 , wherein the carbon black includes FEF carbon black.
4. The power transmission belt of claim 1 , wherein the amount of the organic peroxide is 8 to 12 parts by mass relative to 100 parts by mass of the rubber component.
5. The power transmission belt of claim 1 , wherein the power transmission belt is a V-ribbed belt.
6. The power transmission belt of claim 1 , wherein the power transmission belt is a flat belt.
7. The power transmission belt according to claim 1 , wherein the inner peripheral layer is made of the rubber composition.
8. A power transmission belt used by being wound around a flat pulley so that an inner peripheral surface of the belt contacts with the flat pulley, comprising:
(a) a portion forming the inner peripheral surface made of a rubber composition;
(b) an adhesive rubber layer;
(c) a cord embedded in the adhesive rubber layer; and
(d) an outer peripheral rubber layer attached to the portion (a) through the adhesive layer;
wherein the rubber composition comprises:
100 parts by mass of ethylene-propylene-diene terpolymer as a rubber component,
30 to 70 parts by mass of an unsaturated metal carboxylate salt,
5 to 25 parts by mass of carbon black, and
an organic peroxide as a crosslinker;
wherein the ethylene-propylene-diene terpolymers has a Mooney viscosity ML 1+4 (100° C.) of 30 or more, and an ethylene content of 55 mass % or more;
wherein a total of 35 to 95 parts by mass of the unsaturated metal carboxylate salt and the carbon black are added relative to 100 parts by mass of the rubber component, and an mass ratio of the unsaturated metal carboxylate salt to the carbon black (unsaturated metal carboxylate salt/carbon black) is 1.2/1 to 14/1;
wherein dynamic viscoelasticity properties of the crosslinked rubber composition in a belt length direction satisfy:
((a loss tangent tan δ at a temperature of 25° C. and a dynamic strain of 3.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain 3.0%))×1000<3.0 MPa −1 , and (a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 1.0%)/(a storage elastic modulus E′ at a temperature of 25° C. and a dynamic strain of 3.0%)<1.30.