Supported catalysts for producing ultra-low sulphur fuel oils
The present invention relates to the preparation of catalysts used in the hydrodesulfurization of fossil fuels and proposes a method for preparing thermally stable, low-cost catalysts for the hydrodesulfurization of petrol and diesel, based on highly active CoMo and NiMo. The catalyst for the hydroprocessing of gasoil or petrol in the present invention comprises a precursor which consists of chemical compounds obtained from organic acids and metal salts, and a support containing an ultra-stable Y-type zeolite useful in the hydroprocessing of heavy gas oil and/or light cyclic gas oil with high conversion rates.
1. A catalyst for gasoil or gasoline hydrotreating comprising
a precursor consisting of chemical compounds obtained from organic acids and metal salts selected from the group consisting of metals from Group VI of the periodic table and metals from Group IX or X of the periodic table, and
an alumina-zeolite support comprising an alumina containing ultra-stable Y-type zeolite,
wherein the precursor is a bimetallic organometallic complex with 12 to 15% by weight of the Group VI metal and 2.8 to 4.5% by weight of the Group IX or X metal, and
wherein the alumina-zeolite support has a specific surface area of from 150 to 280 m 2 g −1 .
2. The catalyst according to claim 1 , wherein the metal salts of Group VI of the periodic table is Mo or W.
3. The catalyst according to claim 1 , wherein the organic acids are selected from the group consisting of malic acid, oxalic acid and citric acid.
4. The catalyst according to claim 1 , wherein the metal salts of Group VI of the periodic table are selected from the group consisting of molybdenum trioxide, molybdic acid, ammonium heptamolybdate, equivalent compounds of tungsten.
5. The catalyst according to claim 1 , wherein the support contains from 3 to 20% of the ultra-stable Y-type zeolite.
6. The catalyst according to claim 5 , wherein the support contains from 5 to 10% of the ultra-stable Y-type zeolite.
7. The catalyst according to claim 1 , wherein the support comprises pores and between 60 and 80% of the pores have a pore diameter between 7 and 9 nm.
8. The catalyst according to claim 1 , wherein the support is obtained using nitric acid as chemical agent.
9. The catalyst according to claim 1 , wherein the catalyst has a total metal concentration in the range from 10 to 20% by weight.
10. The catalyst according to claim 9 , wherein the catalyst has a total metal concentration from 12 to 15% of Mo or W and from 3 to 5% of Co or Ni.
11. The catalyst according to claim 1 , wherein it is useful in hydrotreating of a heavy gas oil fraction, with 36000 ppm of S and 1400 ppm of N, at a hydrogen partial pressure from 30 to 50 atm, and temperatures from 300 to 380° C.; or hydrotreating of a light cyclic gasoil fraction, with 22000 ppm of S and 400 ppm of N, at a hydrogen partial pressure from 30 to 35 atm, and temperatures from 300 to 380° C.
12. The catalyst according to claim 1 , wherein it is useful in processing of light organosulfur compounds, intermediate organosulfur compounds, and multisubstituted organosulfur compounds.
13. The catalyst according to claim 12 , wherein the light organosulfur compound is thiophene, the intermediate organosulfur compound is dibenzothiophene, and the multisubstituted organosulfur compound is 4, 6 dimethyl dibenzothiophene.
14. A method of production of the catalyst according to claim 1 for gasoil or gasoline hydrotreating comprising the steps of:
a) depositing bimetallic complexes by support impregnation;
b) drying at a temperature between 90 and 110° C.; and
c) decomposing at a temperature lower than 500° C.
15. The method of production of a catalyst for gasoil or gasoline hydrotreating according to claim 14 , wherein techniques in combination with hydrothermal treatment, wet impregnation and acidic attack are used.
16. The method of production of a catalyst for gasoil or gasoline hydrotreating according to claim 14 , wherein the decomposing is at a temperature between 150-350° C.
17. A catalyst for gasoil or gasoline hydrotreating comprising
a precursor consisting of chemical compounds obtained from organic acids and metal salts; and
an alumina-zeolite support,
wherein the precursor forms nanostructures of Mo(W)S 2 with a stack of 1 to 6 films, with a length between 1 and 3 nm, and wherein the fraction with size from 3 to 6 nm, is found between 40 and 50%.
18. The catalyst according to claim 17 , wherein the Mo(W)S 2 forms nanostructures from 1 to 3 layers with size from 2 to 6 nm, wherein the fraction with size from 6 to 10 nm is between 10 and 15% and wherein the fraction with size from 3 to 6 nm is between 85 and 90%.
19. A catalyst for gasoil or gasoline hydrotreating comprising
a precursor consisting of chemical compounds obtained from organic acids and metal salts; and
an alumina-zeolite support,
wherein the support has a specific surface area from 280 to 680 m 2 g −1 , a pore volume from 0.4 to 0.9 cm×g −1 and an average pore diameter from 3 to 10 nm.