Hybrid cord consisting of at least two multifilament yarns twisted together
A hybrid cord of at least two multifilament yarns twisted together is described, where the first yarn is a viscose multifilament yarn and the second yarn is a non-metallic multifilament yarn composed of a material that is not identical to the first multifilament yarn. The viscose multifilament yarn is conditioned in the standard climate in accordance with DIN EN ISO 139-1:2005, and has a yarn linear density <1100 dtex and a breaking tenacity of ≧45 cN/tex. The hybrid cord has a cord linear density of ≦3000 dtex.
1. A hybrid cord comprising at least two multifilament yarns twisted together, wherein:
a first yarn is a viscose multifilament yarn;
a second yarn is a non-metallic multifilament yarn composed of a material that is not identical to the first yarn;
the viscose multifilament yarn has been conditioned in a standard climate in accordance with DIN EN ISO 139:2011-10 and has a yarn linear density <1100 dtex and a breaking tenacity of ≧45 cN/tex; and
the hybrid cord has a cord linear density of ≦3000 dtex.
2. The hybrid cord according to claim 1 , wherein the second yarn has a yarn linear density in the range from ≧50 to ≦1800 dtex.
3. The hybrid cord according to claim 1 , wherein the hybrid cord has a cord linear density ≦2500 dtex.
4. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has a yarn linear density in the range from ≧150 dtex to ≦1100 dtex.
5. The hybrid cord according to claim 4 , wherein the viscose multifilament yarn has a yarn linear density in the range from ≧200 dtex to <800 dtex and a breaking tenacity in the range from ≧45 cN/tex to ≦53 cN/tex.
6. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has a filament linear density in the range from 1.2 to 4.0 dtex.
7. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has an elongation at break in the range from ≧5% to ≦20%.
8. The hybrid cord according to claim 1 , wherein the second yarn is an aramid multifilament yarn or a polyamide multifilament yarn.
9. The hybrid cord according to claim 1 , wherein the second yarn is a polyester multifilament yarn.
10. The hybrid cord according to claim 1 , wherein the second yarn has a yarn linear density in the range from ≧250 to ≦800 dtex.
11. The hybrid cord according to claim 1 , wherein:
the first yarn is a rayon multifilament yarn;
the second yarn is a PA66 multifilament yarn; and
the hybrid cord has the construction rayon 780×1+PA66 700×1.
12. The hybrid cord according to claim 1 , wherein:
the first yarn is a rayon multifilament yarn;
the second yarn is an aramid multifilament yarn; and
the hybrid cord has the construction rayon 620×1+aramid 550×1.
13. The hybrid cord according to claim 12 , further comprising
a third multifilament yarn that is a rayon multifilament yarn identical to the first yarn, wherein
the hybrid cord has the construction rayon 620×1+aramid 550×1+rayon 620×1.
14. The hybrid cord according to claim 1 , wherein the second yarn has a yarn linear density in the range from ≧200 to ≦1200 dtex.
15. The hybrid cord according to claim 1 , wherein the hybrid cord has a cord linear density ≦2000 dtex.
16. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has a yarn linear density in the range from ≧170 dtex to <900 dtex and a breaking tenacity in the range from ≧45 cN/tex to ≦60 cN/tex.
17. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has a yarn linear density in the range from ≧170 dtex to <900 dtex and a breaking tenacity in the range from ≧45 cN/tex to ≦56 cN/tex.
18. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has a filament linear density in the range from 2.4 to 3.0 dtex.
19. The hybrid cord according to claim 1 , wherein the viscose multifilament yarn has an elongation at break in the range from ≧6% to ≦15%.
20. The hybrid cord according to claim 1 , wherein the second yarn is a PA66 multifilament yarn.
21. The hybrid cord according to claim 1 , wherein the second yarn is a PET multifilament yarn.
22. The hybrid cord according to claim 1 , wherein the second yarn is a high-modulus low-shrinkage PET multifilament yarn.
23. The hybrid cord according to claim 1 , wherein:
the first viscose multifilament yarn is a rayon multifilament yarn;
the second yarn is a PA66 multifilament yarn; and
the hybrid cord has the construction rayon 780×1+PA66 700×1 twisted with 450 tpm S(Z)+450 tpm S(Z), 450 tpm Z(S).
24. The hybrid cord according to claim 1 , wherein:
the first yarn is a rayon multifilament yarn;
the second yarn is an aramid multifilament yarn; and
the hybrid cord has the construction rayon 620×1+aramid 550×1 twisted with 600 tpm S(Z)+600 tpm S(Z), 600 tpm Z(S).
25. The hybrid cord according to claim 12 , comprising
a third multifilament yarn being a rayon multifilament yarn identical to the first yarn, wherein
the hybrid cord has the construction rayon 620×1+aramid 550×1+rayon 620×1 twisted with 600 tpm S(Z)+600 tpm S(Z), 600 tpm Z(S).