Thermal stability of copper-manganese spinel as Zero PGM catalyst for TWC application
Effect of the type of ZPGM material composition to improve thermal stability of ZPGM catalyst systems for TWC application is disclosed. ZPGM catalyst system samples are prepared and configured with washcoat on ceramic substrate, overcoat including doped Zirconia support oxide, and impregnation layer including either Cu 1 Mn 2 O 4 spinel or Cu 1 Co 1 Mn 1 O 4 spinel. Testing of ZPGM catalyst samples including variations of aging temperatures and different impregnation layer materials are developed under isothermal steady state sweep test condition for ZPGM catalyst systems to evaluate performance especially NO x conversions and level of thermal stability. As a result disclosed ZPGM catalyst systems with most suitable spinel that includes Cu 1 Co 1 Mn 1 O 4 in impregnation layer exhibit high NOx conversion and significant improved thermal stability compare to Cu 1 Mn 2 O 4 spinel, which is suitable for under floor and close coupled TWC application. The effect of adding Co to Cu—Mn spinel composition to improve thermal stability confirmed by TPR measurement.
1. A zero platinum group metal (ZPGM) catalyst system comprising:
a substrate,
a washcoat layer overlying the substrate,
an overcoat layer overlying the washcoat layer, said overcoat layer consisting of ZrO 2 —Pr 6 O 11 , and
an impregnation layer deposited on a surface of the overcoat layer;
wherein the impregnation layer comprises a spinel according to the formula Cu x Mn 3-x O 4 or Cu x Co y Mn 3-x-y O 4 , wherein X and Y are each independently 0.01 to 1.0, wherein the catalyst system has been aged at about 850° C.
2. The ZPGM catalyst system of claim 1 , wherein the substrate is ceramic.
3. The ZPGM catalyst system of claim 1 , wherein the impregnation layer comprises CuMn 2 O 4 spinel.
4. The ZPGM catalyst system of claim 1 , wherein the impregnation layer comprises CuCoMnO 4 spinel.
5. The ZPGM catalyst system of claim 4 , wherein the spinel is stable up to about 1040° C.
6. The ZPGM catalyst system of claim 1 , wherein the washcoat layer is an alumina-based washcoat on substrate.
7. The ZPGM catalyst system of claim 1 , wherein the spinel is aged under fuel cut gas conditions.
8. The ZPGM catalyst system of claim 1 , wherein nitrogen oxide (NOx) conversion is about 52% to about 98% when having an R-value of 1.2 under an isothermal steady state sweep condition.
9. A method of producing an aged zero platinum group metal (ZPGM) catalyst system comprising aging the catalyst system of claim 1 at a temperature of about 850° C.
10. The method of claim 9 , wherein the aging lasts about 20 hours.
11. The method of claim 9 , wherein the impregnation layer comprises CuMn 2 O 4 spinel.
12. The method of claim 9 , wherein the impregnation layer comprises CuCoMnO 4 spinel.
13. The method of claim 12 , wherein the aged ZPGM catalyst system converts nitrogen oxide (NOx) at about 52% to about 98% when having an R-value of 1.2 under an isothermal steady state sweep condition.