Method and device for transfer lamination
View Patent ↗A transfer laminate ( 35 ), comprising a carrier film having an adhering decorative element having a solid, pigmented, partially cured decorative layer, is laminated on the decoration side onto a substrate ( 40 ) having a temperature between 50 and 70° C. on the decoration side, on which substrate a coating that can be painted over has been applied in the course of a traditional process. The paint layer of the coating that was applied last is still moist and tacky after the intermediate drying thereof. The transfer laminate ( 35 ) is laminated onto the still moist and tacky paint layer on the substrate ( 40 ), and at least the region of the transfer laminate ( 35 ) containing the decorative element is pressed onto the substrate coating over the entire area at a pressure of 0.2 to 5.0 bar for 40 to 240 seconds. Then the carrier film is quickly cooled to a temperature less than 20° C. and then removed from the substrate coating, wherein the decorative element remains on the substrate coating. The device for transfer lamination forms an applicator ( 10 ), which comprises: two flexible membranes ( 20, 22 ), which are both clamped pressure-tight on a common frame ( 12 ) along the perimeter of the membranes in such a way that an intermediate space is created therebetween, in which a flexible warm—or hot-water layer ( 27 ) can be enclosed; a chamber ( 30 ), which can be filled with compressed air, wherein overall such an arrangement is created that a gradual introduction of compressed air into the chamber ( 30 ) moves the two flexible membranes ( 20, 22 ) and the flexible warm—or hot-water layer ( 27 ) jointly in the manner of a balloon onto the substrate surface ( 42 ) to be coated in order to apply the transfer laminate ( 35 ) to and press the transfer laminate onto said substrate surface ( 42 ) without bubbles.
1. A method for transfer lamination
in which a transfer laminate, comprising a backing foil with an adhering decorative element having a solid, pigmented, partially cured decorative layer,
is laminated by its decoration side onto a substrate, and
finally the backing foil is peeled off and removed,
wherein
a substrate is provided, having a temperature of 50 to 70° C., to which an overpaintable coating has been applied in the course of a conventional painting operation, the coating comprising a paint film that has been applied last and being still moist and tacky after its interim drying;
the transfer laminate is laminated onto the still moist and tacky paint film on the substrate; and
at least the region of the transfer laminate that comprises the decorative element is pressed onto the substrate coating for 40 to 240 sec over its full area under a pressure of 0.2 to 5.0 bar, more particularly under a pressure of 0.4 to 5.0 bar; and
toward the end of the pressing phase, the backing foil is cooled rapidly to a temperature of 5 to 20° C. and
is thereafter removed from the decorative layer and, optionally, substrate coating, the decorative element remaining on the substrate coating; and
the substrate coating with the transferred decorative layer is cured completely.
2. The method for transfer lamination as claimed in claim 1 , wherein
the transfer laminate is heated to a temperature in the range from 60 to 95° C. and at this temperature is laminated onto the still moist and tacky paint film on the substrate.
3. The method for transfer lamination as claimed in claim 1 , wherein
the overpaintable coating on the substrate is a pigmented basecoat film or top film, whose crosslinking has been initiated but not yet concluded.
4. The method for transfer lamination as claimed in claim 1 , wherein
the backing foil is a polymeric foil
which consists of polyolefin, halogenated polyolefin, polyamide, or aromatic polyester, and also of mixtures and/or blends of these materials; and
the polymeric foil has a layer thickness of 10 to 250 μm.
5. The method for transfer lamination as claimed in claim 1 wherein
the decorative layer is obtainable from thermosetting paint formulations based on chemically reactive acrylate resins whose urethane-forming crosslinking reaction can be initiated even by moderate heating to a temperature of 60 to 80° C.
6. The method for transfer lamination as claimed in claim 1 , wherein
the decorative layer is obtainable from thermosetting paint formulations based on chemically reactive acrylate resins whose urethane-forming crosslinking reaction can be initiated even by moderate heating to a temperature of 60 to 80° C.;
a substrate is provided, having a temperature of 50 to 70° C., to which an overpaintable coating has been applied in the course of a conventional painting operation, coating comprising a basecoat film that has been applied and being still moist and tacky after its interim drying;
the transfer laminate is heated to a temperature of 60 to 95° C. and is laminated at that temperature onto the still moist and tacky basecoat film on the substrate; and
at least the region of the transfer laminate that comprises the decorative element is pressed onto the substrate coating for 40 to 240 sec over its full area under a pressure of 0.4 to 5.0 bar; and
toward the end of the pressing phase, the backing foil is cooled rapidly to a temperature of 5 to 20° C. and
is thereafter removed from the decorative layer and, optionally, substrate coating, the decorative element remaining on the substrate coating; and
the substrate coating with the transferred decorative layer is cured completely.
7. The method for transfer lamination as claimed in claim 1 , wherein
the decorative layer has a dry layer thickness of 18 to 30 μm.
8. The method for transfer lamination as claimed in claim 1 , wherein
the substrate is a comparatively extensive automotive bodywork part;
the overpaintable substrate coating is a freshly produced film, still moist and tacky after brief interim drying, composed of a pigmented waterborne basecoat material; and
the transfer laminate provided with the heated and overpaintable decorative layer is pressed onto the overpaintable substrate coating under a pressure of 0.5 to 0.8 bar.
9. The method for transfer lamination as claimed in claim 1 , wherein
the backing foil, lying with its lay-on temperature on the substrate coating, is cooled within a timespan of less than 30 sec to a temperature of less than 20° C.
10. The method for transfer lamination as claimed in claim 1 , wherein
the substrate coating provided with the transferred decorative layer—optionally after additional application of a clearcoat film—is completely cured by drying at a temperature of 130 to 150° C.