Self-healing dental restorative formulations and related methods
Dental restorative formulations comprising an additive material and a capsule incorporated into the continuous phase of a dental material. The additive material includes one or more alkoxy groups and one or more vinyl groups. The capsule includes a catalyst and a molecule with one or more silanol groups. The dental restorative formulation is applied and polymerized to form a composite. When a disturbance occurs in the dental composite, the capsule ruptures so that the catalyst initiates a condensation reaction between the molecule with one or more silanol groups and the one or more alkoxy groups thereby healing the dental composite.
1. A dental restorative formulation, comprising:
a dental material and a continuous phase of said dental material,
wherein said dental material includes a precursor matrix comprising one or more di-acrylate monomers selected from the group consisting of 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy) phenyl]propane (“Bis-GMA”), dimethacryloxyethyl 2,2,4-trimethylhexamethylene diurethane (“UDMA”), triethyleneglycol dimethacrylate (“TEGDMA”), and combinations thereof, and an additive material; and wherein said dental material includes a filler comprising a capsule, wherein said additive material includes one or more alkoxy groups and one or more vinyl groups, and the capsule comprising a catalyst and a molecule, wherein said molecule includes one or more silanol groups, wherein,
the dental restorative formulation is polymerized with the di-acrylate monomers wherein the vinyl group reacts with the dental monomer in the precursor matrix to form the continuous phase of a composite and upon the occurrence of a disturbance in the composite said capsule ruptures such that said catalyst initiates a condensation reaction to polymerize said additive material wherein one or more silanol groups of said molecule is reactive with one or more of said alkoxy functional group of said additive material to form silyl ether linkages, thereby healing the dental composite.
2. The dental restorative formulation of claim 1 , wherein said additive material is vinylethoxysiloxane.
3. The dental restorative formulation of claim 2 , wherein said vinylethoxysiloxane is oligomeric.
4. The dental restorative formulation of claim 2 , wherein said vinylethoxysiloxane is polymeric.
5. The dental restorative formulation of claim 2 , wherein said vinylethoxysiloxane is monomeric.
6. The dental restorative formulation of claim 1 , wherein said catalyst is tin (II) ethylhexanoate.
7. The dental restorative formulation of claim 1 , wherein said capsule accounts for about 1-15 wt % of the dental restorative formulation.
8. The dental restorative formulation of claim 1 , wherein said additive material accounts for 1-15 wt % of the dental restorative formulation.
9. The dental restorative formulation of claim 1 , wherein said catalyst includes at least one of organotin catalysts including at least one of stannous octooate, dialkyl dicarboxylate or dibutyl tin dilaurate, and platinum compounds including at least one of chloroplatinic acid or hydride-functional siloxanes.
10. A method of forming a dental composite, comprising the steps of:
combining a dental material including a precursor matrix comprising one or more di-acrylate monomers selected from the group consisting of Bis-GMA, UDMA, TEGDMA, or combinations thereof and a continuous phase of said dental material including an additive material and a capsule, wherein the additive material includes one or more alkoxy groups and one or more vinyl groups, and the capsule comprising a catalyst and a molecule including one or more silanol groups to form a dental restorative formulation;
applying the dental restorative formulation to at least one of a tooth or dental structure;
polymerizing the di-acrylate monomers in the dental restorative formulation to form a dental composite; and
wherein rupture of the capsule results in the catalyst initiating a condensation reaction between the molecule and the additive material whereby forming silyl ether linkages to heal the dental composite.