Thin film transistor, array substrate and display device having the same, and method of manufacturing thereof
The disclosure provides a method of manufacturing a thin film transistor on a base substrate by patterning an active layer comprising a metal oxynitride, and treating the active layer with a plasma comprising oxygen.
1. A method of manufacturing a bottom gate type thin film transistor on a base substrate, comprising:
forming an active layer comprising a metal oxynitride;
forming an etching stop layer on top of the active layer pattern; and
subsequent to forming the etching stop layer, treating the active layer with a plasma comprising oxygen.
2. The method according to claim 1 , wherein the method further comprising, following the step of treating the active layer with a plasma comprising oxygen,
depositing a source-drain electrode layer on top of the etching stop layer;
annealing a substrate having the source-drain electrode layer; and
patterning the source-drain electrode layer.
3. The method according to claim 1 , wherein the treating step comprises plasma bombarding the active layer with a plasma comprising oxygen.
4. The method according to claim 1 , wherein a gas is used for treating the active layer, wherein the gas comprises oxygen or nitrous oxide.
5. The method according to claim 4 , wherein the pressure of the gas for treating the active layer ranges from 200 to 2000 mTor, and the treating time ranges from 10 to 200 seconds.
6. The method according to claim 2 , wherein atmosphere for annealing the substrate comprises nitrogen or an inert gas.
7. The method according to claim 6 , wherein the temperature for annealing the substrate ranges from 200 to 400 Celsius, and the time for annealing the substrate ranges from 20 to 60 minutes.
8. The method according to claim 1 , wherein the active layer comprises Zinc Oxynitride.
9. The method according to claim 1 , wherein the active layer further comprises an element X in the Zinc Oxynitride, the element X is selected from the group consisting of the following or combination thereof: boron, aluminum, gallium, indium, tin, titanium, zirconium, hafnium, silicon, fluorine, chlorine, bromine, iodine, sulfur, and selenium.
10. The method according to claim 1 , wherein the turn-off current of the thin film transistor is at least 100 times lower than the on/off ratio of an untreated thin film transistor.
11. An array substrate manufactured according to the method of claim 1 .
12. A display device comprising the array substrate of claim 11 .
13. A method of manufacturing a top gate type thin film transistor on a base substrate, comprising forming an active layer comprising a metal oxynitride; treating the active layer with a plasma comprising oxygen; and subsequent to treating the active layer with a plasma comprising oxygen, annealing a substrate comprising the active layer.
14. The method according to claim 13 , wherein atmosphere for annealing the substrate comprises nitrogen or an inert gas.