Method for coating a sliding element and sliding element, in particular a piston ring or cylinder liner of an internal combustion engine
In a method for coating a sliding element, in particular a piston ring or a cylinder liner of an internal combustion engine, DLC phases are embedded into a hard material layer as said hard material layer is deposited. A sliding element, such as a piston ring or a cylinder liner of an internal combustion engine, comprises a hard material layer with embedded DLC phases.
1. A coated sliding element comprising a sliding element and a hard material layer, the hard material layer comprises chromium nitride (CrN) with diamond-like carbon (DLC) phases embedded therein, wherein the CrN with the DLC phases embedded therein forms the outermost surface of the coated sliding element,
wherein the content of the DLC phases is increased at the outermost surface and/or in the uppermost 1 to 2 microns of the hard material layer as compared to the remaining portion of the layer, and wherein the sliding element is a piston ring or a cylinder liner for an internal combustion engine.
2. The sliding element according to claim 1 , wherein the hard material layer has a thickness of ≧10 μm.
3. The sliding element according to claim 1 , wherein the hard material layer furthermore contains at least one additional element selected from the group of: boron, carbon, oxygen, and silicon.
4. The sliding element according to claim 3 , wherein the hard material layer contains boron.
5. The sliding element according to claim 1 , wherein the embedded DLC phases are uniformly distributed in a portion below the outermost surface and/or below the uppermost 1 to 2 μm of the hard material layer.
6. The sliding element according to claim 1 , wherein the DLC phases have a content between 0.1 and 99.9%.
7. The sliding element according to claim 1 , wherein an area of the hard material layer located in the uppermost 1 to 2 μm of the hard material layer includes the DLC phases in an amount up to 100%.
8. The sliding element according to claim 1 , wherein the DLC phases have a content that varies via the layer thickness.
9. A coated sliding element comprising a sliding element and a hard material layer, wherein the hard material layer forms an outermost surface of the coated sliding element and the hard material layer consist essentially of chromium nitride (CrN) with diamond-like carbon (DLC) phases embedded therein;
wherein the content of DLC phases is increased at the outermost surface and/or in the uppermost 1 to 2 microns of the hard material layer as compared to the remaining portion of the layer, and wherein the sliding element is a piston ring or a cylinder liner for an internal combustion engine.