Sewn airbag and method for producing the same
A sewn airbag includes a plurality of base fabrics sewn together, wherein in a sewn region where reinforcement is required, a reinforcing coating film made of an adhesive coating material that is adhesive to both a sewing yarn and fibers forming the base fabrics is formed on at least one of the upper and lower surfaces of the sewn region, the reinforcing coating film having the smallest possible width along a stitching region in the form of one or more strips forming the sewn region made with the sewing yarn.
1. A sewn airbag comprising a plurality of base fabrics sewn together, wherein
in a sewn region where reinforcement is required, a reinforcing coating film made of an adhesive coating material that is adhesive to both a sewing yarn and fibers forming the base fabrics is formed on at least one of the upper and lower surfaces of the sewn region, the reinforcing coating film having the smallest possible width along a stitching region in the form of one or more strips forming the sewn region made with the sewing yarn.
2. The sewn airbag according to claim 1 , wherein
the base fabrics are non-coated base fabrics or single-coated base fabrics.
3. The sewn airbag according to claim 1 , wherein
the adhesive coating material is a urethane-based emulsion coating material.
4. The sewn airbag according to claim 1 , wherein
the adhesive coating material is a carbonate-modified-urethane-based emulsion coating material.
5. The sewn airbag according to claim 4 , wherein
the adhesive coating material further contains a carbodiimide compound as a crosslinking agent.
6. The sewn airbag according to claim 2 , wherein
the reinforcing coating film has a width of 3 mm or more on one side, and the coating weight of the adhesive coating material on solid basis is 3 to 80 g/m 2 .
7. The sewn airbag according to claim 2 , wherein
the base fabrics have a cover factor (CF) within a range of 1500 to 2500 as determined by the following equation (1):
CF= NW×DW 0.5 +NF×DF 0.5 (1)
wherein
NW: warp density (the number of yarns/inch), DW: warp fineness (dtex)
NF: weft density (the number of yarns/inch), DF: weft fineness (dtex).
8. The sewn airbag according to claim 1 , wherein
the slippage resistance of the sewing yarn after the formation of the reinforcing coating film is 1.3 times or more higher than before the formation of the coating film.
9. The sewn airbag according to claim 1 , wherein
the slippage resistance of the sewing yarn after the formation of the reinforcing coating film is 1.5 times or more higher than before the formation of the coating film.