Polyglycolic acid molded article, component for downhole tool, and method of producing polyglycolic acid molded article
The polyglycolic acid having a content of low molecular weight substance of less than 1% by weight; and a molded article thereof having a thickness of 2 mm or greater, the time at which immersion of the molded article in water at 66° C. is started to the time at which the polyglycolic acid decomposed by the water starts to elute being 1 hour or longer by 30 hours or shorter, and a rate of embrittlement, at which embrittlement proceeds due to the elution of the polyglycolic acid, being 0.025 mm/h or greater.
1. A polyglycolic acid molded article comprising polyglycolic acid;
the polyglycolic acid having a content of low molecular weight substance of less than 1% by weight;
the polyglycolic acid molded article having a thickness of 2 mm or greater,
the time at which immersion of the polyglycolic acid molded article in water at 66° C. is started to the time at which the polyglycolic acid decomposed by the water starts to elute being 1 hour or longer but 30 hours or shorter, and
a rate of embrittlement, at which embrittlement of the polyglycolic acid proceeds in a thickness direction from a surface part to a center part of the polyglycolic acid molded article due the elution of the polyglycolic acid, being 0.025 mm/h or greater.
2. The polyglycolic acid molded article according to claim 1 , wherein weight average molecular weights of the polyglycolic acids in the surface part and the center part of the polyglycolic acid molded article are in a range of 70,000 to 150,000.
3. The polyglycolic acid molded article according to claim 2 , wherein a difference between a weight average molecular weight of the polyglycolic acid in the surface part and a weight average molecular weight of the polyglycolic acid in the center part of the polyglycolic acid molded article is 30,000 or less.
4. The polyglycolic acid molded article according to claim 1 , wherein the polyglycolic acid molded article is irradiated with radiation.
5. The polyglycolic acid molded article according to claim 4 , wherein the radiation irradiated to the polyglycolic acid molded article is an electron beam or γ-ray.
6. The polyglycolic acid molded article according to claim 4 , wherein the polyglycolic acid molded article is subjected to hydrothermal treatment by being immersed in hot water before or after irradiation of the radiation.
7. A component for a downhole tool comprising the polyglycolic acid molded article described in claim 1 .