Cathode active material for lithium secondary battery, method of fabricating the same, and lithium secondary battery including the same
Provided are a cathode active material for a lithium secondary battery, a method of fabricating the same, and a lithium secondary battery including the same. The cathode active material includes a lithium composite transition metal oxide represented by Li 1+(c-a)/2 Ni a Co b Mn c O 2-x F x (0.1≦c−a≦0.4, 0.13≦a≦0.3, 0.03≦b≦0.2, 0.4≦c≦0.6, (a+b+c)+(1+(c−a)/2)=2, 0<x≦0.15, 1≦a/b≦6, 1.9≦c/a≦4.0, and 0.04≦b/(a+b+c)≦0.25), and layer-structured Li 2 MnO 3 . Since the lithium secondary battery including the cathode active material has a large capacity and generates less gas, lifespan characteristics and high rate capability are significantly improved, and especially voltage variation during charging and discharging operations is small.
1. A cathode active material, comprising a lithium composite transition metal oxide represented by Li 1+(c-a)/2 Ni a Co b Mn c O 2-x F x (0.1≦c−a≦0.4, 0.13≦a≦0.3, 0.03≦b≦0.2, 0.4≦c≦0.6, (a+b+c)+(1+(c−a)/2)=2, 0<x≦0.15, 1≦a/b≦6, 1.9≦c/a≦4.0, and 0.04≦b/(a+b+c)≦0.25), wherein the lithium composite transition metal oxide includes layer-structured Li 2 MnO 3 .
2. The cathode active material of claim 1 , wherein a specific surface area is 3 to 10 m 2 /g.
3. The cathode active material of claim 1 , wherein an average diameter of secondary particles is 2 to 5 μm, and an average diameter of primary particles is 50 to 500 nm.
4. The cathode active material of claim 1 , wherein the cathode active material is a mixture of a rhombohedral material and a monoclinic material.
5. A method of fabricating the cathode active material described in claim 1 , comprising:
providing a composite transition metal hydroxide represented by an empirical formula of Ni a′ Co b′ Mn c′ (OH) 2 (0.15≦a′<0.354, 0.036≦b′<0.24, 0.48≦c′<0.72, and a′+b′+c′=1); and
mixing the composite transition metal hydroxide, a lithium source, and a fluorine source and performing a heat treatment at 600 to 800° C.
6. The method of claim 5 , wherein the lithium source is one or more selected from the group consisting of Li 2 CO 3 , LiOH, LiNO 3 , LiCH 3 COO, and a mixture thereof.
7. The method of claim 5 , wherein the fluorine source is one or more selected from the group consisting of LiF, NH 4 F, NaF, KF, CsF, RbF, TiF, AgF, AgF□, BaF 2 , CaF 2 , CuF 2 , CdF 2 , FeF 2 , HgF 2 , Hg 2 F 2 , MnF 2 , MgF 2 , NiF 2 , PbF 2 , SnF 2 , SrF 2 , XeF 2 , ZnF 2 , AlF 3 , BF 3 , BiF 3 , CeF 3 , CrF 3 , DyF 3 , EuF 3 , GaF 3 , GdF 3 , FeF 3 , HoF 3 , InF 3 , LaF 3 , LuF 3 , MnF 3 , NdF 3 , VOF 3 , PrF 3 , SbF 3 , ScF 3 , SmF 3 , TbF 3 , TiF 3 , TmF 3 , YF 3 , YbF 3 , TIF 3 , CeF 4 , GeF 4 , HfF 4 , SiF 4 , SnF 4 , TiF 4 , VF 4 , ZrF 4 , NbF 5 , SbF 5 , TaF 5 , BiF 5 , MoF 6 , ReF 6 , SF 6 , WF 6 , and a mixture thereof.
8. A lithium second battery comprising the cathode active material described in any one of claim 1 .