View Patent ↗To provide an ink-jet white ink of active energy ray-curable type, wherein the white ink has high printing stability and good hiding property, and is particularly suitable for printing on the single-pass ink-jet printing system. An ink-jet white ink of active energy ray-curable type, comprising titanium oxide, a pigment dispersant, and a polymerizable compound, wherein the content of the titanium oxide is from 15 to 30% by weight with reference to the total weight of the ink, and wherein the weight average particle diameter of the titanium oxide is 180 to 250 nm. In an embodiment of the ink, the titanium oxide is titanium oxide that surface is treated with silica and the pigment dispersant comprises a basic dispersant.
1. An ink, for printing on a single-pass ink-jet printing system said ink comprising titanium oxide, a basic dispersant as a pigment dispersant, and a polymerizable compound,
wherein a content of the titanium oxide is from 19 to 30% by weight with reference to a total weight of the ink, and
wherein a weight average particle diameter of the titanium oxide is from 180 to 250 nm, and
wherein the titanium oxide is a titanium oxide whose surface is treated with at least silica.
2. The ink of claim 1 , wherein the titanium oxide has hydroxyl groups on treated surface thereof.
3. The ink of claim 1 , wherein the polymerizable compound comprises at least one of the polymerizable compounds of formulae (1) and (2):
wherein R 1 and R 2 are each independently a hydrogen atom or a methyl group, R 3 is a hydrogen atom or an alkyl group with 1 to 10 carbon atoms, and n is an integer of 1 to 10,
wherein R 1 is a hydrogen atom or a methyl group, R 3 is a hydrogen atom or an alkyl group with 1 to 10 carbon atoms, and m is an integer of 1 to 10.
4. The ink of claim 1 , further comprising a polymerization initiator, wherein the polymerization initiator comprises at least one selected from the group consisting of 2,4,6-trimethylbenzoyl diphenyl phosphine oxide, bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide, and 4-benzoyl-4′-methyldiphenyl sulfide.
5. The ink of claim 1 , further comprising an organic solvent, wherein a content of the organic solvent is from 0.01 to 5% by weight with reference to the total weight of the ink.
6. The ink of claim 1 , wherein the titanium oxide is present in the ink in an amount of from 19 to 25% by weight with reference to the total weight of the ink.
7. The ink of claim 1 , wherein the titanium oxide is titanium oxide whose surface is treated with an aluminum compound and silica.
8. The ink of claim 1 , wherein the polymerizable compound comprises at least one selected from the group consisting of lauryl acrylate, dipropylene glycol diacrylate, N-vinyl caprolactam, 1,9-nonanediol diacrylate, and 1,10-decanediol diacrylate.
9. The ink of claim 3 , wherein the polymerizable compound comprises at least one selected from the group consisting of lauryl acrylate, dipropylene glycol diacrylate, N-vinyl caprolactam, 1,9-nonanediol diacrylate, and 1,10-decanediol diacrylate.