Crosslinking resin composition and sealing material
The present invention provides a crosslinking resin composition comprising an ethylene copolymer and a crosslinking aid, in which the crosslinked product of the resin composition has excellent insulation properties (volume resistivity value). The present invention provides a heat-crosslinking resin composition comprising an ethylene copolymer, a crosslinking agent and a urethane poly(meth)acrylate as a crosslinking aid, and (2) a radiation-crosslinking resin composition comprising an ethylene copolymer and a urethane poly(meth)acrylate as a crosslinking aid.
1. A solar cell comprising a sealing material consisting of a heat-crosslinkable resin composition consisting of:
an ethylene copolymer selected from the group consisting of ethylene-vinyl acetate copolymers, ethylene-unsaturated carboxylic acid ester copolymers, and mixtures thereof,
an organic peroxide as a crosslinking agent, and
a urethane poly(meth)acrylate as a crosslinking aid,
wherein:
an amount of the urethane poly(meth)acrylate in the heat-crosslinkable resin composition
is 0.1 to 2.0 parts by weight based on 100 parts by weight of the ethylene copolymer;
an amount of the organic peroxide in the heat-crosslinkable resin composition is 0.6 to 2.0 parts by weight based on 100 parts by weight of the ethylene copolymer; and
the average molecular weight of the urethane poly(meth)acrylate is not less than 1000.
2. A solar cell comprising a sealing material consisting of a heat-crosslinkable resin composition consisting of
an ethylene copolymer selected from the group consisting of ethylene-vinyl acetate copolymers, ethylene-unsaturated carboxylic acid ester copolymers, and mixtures thereof,
an organic peroxide as a crosslinking agent,
a urethane poly(meth)acrylate as a crosslinking aid, and
at least one additive selected from the group consisting of reinforcing agents, plasticizers, processing aids, lubricants, pigments, anti-aging agents, coupling agents, and acid acceptors,
wherein:
an amount of the urethane poly(meth)acrylate in the heat-crosslinkable resin composition
is 0.1 to 2.0 parts by weight based on 100 parts by weight of the ethylene copolymer;
an amount of the organic peroxide in the heat-crosslinkable resin composition is 0.6 to 2.0 parts by weight based on 100 parts by weight of the ethylene copolymer; and
the average molecular weight of the urethane poly(meth)acrylate is not less than 1000.