Coextruded polyethylene film
A coextruded polyethylene blown film, particularly for packaging, has a thickness between 20 μm and 250 μm and is formed by a foamed, particle-containing core layer between a first unfoamed weldable outer layer and a second unfoamed outer layer. The core layer has a polyethylene or a polyethylene-based mixture as a polymer component having a melt mass-flow rate (MFR) per DIN ISO EN 1133 of greater than 5 g/10 min at 190° C. and 2.16 kg.
1. A coextruded polyethylene blown film for packaging and with a thickness between 20 μm and 250 μm, the film comprising:
a first unfoamed weldable outer layer;
a second unfoamed outer layer, the outer layers each of a polyethylene or a polyethylene-based mixture as a polymer component having a melt mass-flow rate (MFR) per DIN ISO EN 1133 of less than 3 g/10 min; and
a foamed, particle-containing core layer of a polyethylene or a polyethylene-based mixture as a polymer component having a melt mass-flow rate (MFR) per DIN ISO EN 1133 of greater than 5 g/10 min at 190° C. and 2.16 kg.
2. The coextruded polyethylene blown film defined in claim 1 , wherein the mass-flow rate of the outer layers is less than 1 g/10 min at 190° C. and 2.16 kg.
3. The coextruded polyethylene blown film defined in claim 1 , wherein the first outer layer has a higher melt mass-flow rate (MFR) than the second outer layer.
4. The coextruded polyethylene blown film defined in claim 1 , wherein the foamed core layer has closed cells filled with nitrogen or carbon dioxide.
5. The coextruded polyethylene blown film defined in claim 1 , wherein the foamed core layer has closed cells with a volume of less than 50000 μm 3 .
6. The coextruded polyethylene blown film defined in claim 1 , wherein the core layer has a density between 0.2 g/cm 3 and 0.8 g/cm 3 .
7. The coextruded polyethylene blown film defined in claim 1 , wherein the thickness of the foamed core layer is between 40% and 70% of a total thickness of the blown film.
8. The coextruded polyethylene blown film defined in claim 1 , wherein the polymer component of the core layer contains a linear polyethylene as the main component.
9. The coextruded polyethylene blown film defined in claim 8 wherein the polymer component includes metallocene catalysts.
10. The coextruded polyethylene blown film defined in claim 8 , wherein the polymer component of the core layer contains at least one other low-density polyethylene besides the linear polyethylene.
11. The coextruded polyethylene blown film defined in claim 1 , wherein the outer layers are immediately adjacent and flank the core layer.
12. The coextruded polyethylene blown film defined in claim 1 , wherein at least one of the outer layers contains colored particles.
13. The coextruded polyethylene blown film defined in claim 1 , wherein the second outer layer has a matte surface with a reflectometer value per DIN 67530 of less than 40 at an angle of measurement of 85°.