Composition for use in decreasing the transmission of human pathogens

1. A facial mask that decreases the transmission of one or more than one human pathogen by antibacterial, antifungal and antiviral activity, the facial mask comprising a wearable facial mask configured for placement over a mouth and nose, the wearable facial mask having a polypropylene-based material comprising four layers, Layer #1, Layer #2, Layer #3 and Layer #4 oriented from a front surface of the facial mask to a back surface of the facial mask, wherein the back surface of the facial mask is a surface of Layer #4 contacting the face of a wearer, and the front surface of the facial mask opposing to the back surface of the facial mask; wherein Layer #1 is a spunbond nonwoven fabric comprising polypropylene fibers having a density of 45 g/m 2 and having a Layer #1 coating prepared from drying a Layer #1 wet coating formed by coating Layer #1 with a Layer #1 aqueous coating composition comprising 2% by weight of citric acid, 2% by weight of polyvinyl alcohol, and 0.5% by weight of polyoxyethylene (20) sorbitan by the total weight of the Layer #1 aqueous coating composition, Layer #2 is a spunbond nonwoven fabric comprising polypropylene fibers having a density of 45 g/m 2 and having a Layer #2 coating prepared from drying a Layer #2 wet coating formed by coating Layer #2 with a Layer #2 aqueous coating composition comprising 3% by weight of copper acetate and 3% by weight of zinc acetate by the total weight of the Layer #2 aqueous coating composition, Layer #3 is a melt-blown polypropylene fabric comprising polypropylene fibers having a density of 18 g/m 2 , and Layer #4 is a spunbond nonwoven polypropylene fabric comprising polypropylene fibers having a density of 25 g/m 2 .

2. A facial mask for decreasing the transmission of one or more than one human pathogen to and from a human wearer of the facial mask, the facial mask comprising: a) a body comprising a front surface of the body, an opposing back surface of the body, and a perimeter of the body defining a shape of the body, and a central seam, wherein the back surface the body contacting the face of the human wearer and the front surface of the body opposing to the back surface of the body; b) a flap attached to the body at a body-flap junction; the flap comprising a front surface of the flap, an opposing back surface of the flap, and a perimeter of the flap defining a shape of the flap; c) a resilient member attached to the back surface of the flap; d) a deformable strip attached to the body; and e) one or more than one extension attached to the body for securing the facial mask to the head of a wearer; where the perimeter of the body comprises a right lateral edge, a left lateral edge connected to the right lateral edge at a bottom junction of the perimeter, and a top edge connecting the right lateral edge to the left lateral edge; where the perimeter of the flap comprises in continuity, a right vertical side, a right arcuate side, a central curved region, a left arcuate side, a left vertical side, and a base partially forming the body-flap junction and connecting the right vertical side to the left vertical side; where the shape of the flap is an inverted U-shape when looking at the front surface of the body or the back surface of the body with the bottom junction oriented down; where both the body and the flap comprise a material comprising four layers, Layer #1, Layer #2, Layer #3 and Layer #4 oriented from the front surface to the back surface, wherein the back surface is a back surface of Layer #4; and where Layer #1 is a spunbond nonwoven fabric comprising polypropylene fibers having a density of 45 g/m 2 and having a Layer #1 coating prepared from drying a Layer #1 wet coating formed by coating Layer #1 with a Layer #1 aqueous coating composition comprising 2% by weight of citric acid, 2% by weight of polyvinyl alcohol, and 0.5% by weight of polyoxyethylene (20) sorbitan by the total weight of the Layer #1 aqueous coating composition, Layer #2 is a spunbond nonwoven fabric comprising polypropylene fibers having a density of 45 g/m 2 and having a Layer #2 coating prepared from drying a Layer #2 wet coating formed by coating Layer #2 with a Layer #2 aqueous coating composition comprising 3% by weight of copper acetate and 3% by weight zinc acetate by the total weight of the Layer #2 aqueous coating composition, Layer #3 is a melt-blown polypropylene fabric comprising polypropylene fibers having a density of 18 g/m 2 , and Layer #4 is a spunbond nonwoven polypropylene fabric comprising polypropylene fibers having a density of 25 g/m 2 .

3. The facial mask of claim 1 , further comprising one or more than one reactive dye.

4. The facial mask of claim 2 , further comprising one or more than one reactive dye.

5. The facial mask of claim 1 , wherein the Layer #2 aqueous coating composition further comprises 2% by weight of citric acid, 2% by weight of polyvinyl alcohol, and 0.5% by weight of polyoxyethylene (20) sorbitan by the total weight of the Layer #2 aqueous coating composition.

6. The facial mask of claim 2 , wherein the Layer #2 aqueous coating composition further comprises 2% by weight of citric acid, 2% by weight of polyvinyl alcohol, and 0.5% by weight of polyoxyethylene (20) sorbitan by the total weight of the Layer #2 aqueous coating composition.