Method for drying particulate polymers
The present invention relates to a process for drying particulate polymers, comprising the steps of: a) providing a particulate polymer comprising from 60 wt % to 90 wt % of at least one solvent based on the total weight of particulate polymer and solvent, b) mechanically predrying the particulate polymer to a content of the at least one solvent of from 20 wt % to 50 wt % based on the total weight of particulate polymer and solvent, wherein the mechanical predrying in step b) is carried out with a roller press, and c) end-drying the particulate polymer to a content of the at least one solvent of from 0 wt % to 15 wt % based on the total weight of particulate polymer and solvent, wherein the particulate polymer is a polymer comprising repeating units of formulae I, II and/or III The present invention further relates to a process for working up particulate polymers.
1. A process for drying particulate polymers, comprising:
a) mechanically pre-drying a particulate polymer comprising from 60 wt % to 90 wt % of a solvent (S 1 ) based on the total weight of particulate polymer and solvent (S 1 ),
to a content of the solvent (S 1 ) of from 20 wt % to 50 wt % based on the total weight of particulate polymer and solvent (S 1 ), wherein the mechanical pre-drying is carried out with a roller press, and
b) end-drying the particulate polymer to a content of the solvent (S 1 ) of from 0 wt % to 15 wt % based on the total weight of particulate polymer and solvent (S 1 ), wherein the particulate polymer is a polymer comprising repeating units of formulae I, II and/or III
2. The process according to claim 1 , wherein the end-drying is carried out with a fluidized bed dryer.
3. The process according to claim 1 , wherein the solvent (S 1 ) is water.
4. The process according to claim 1 , wherein the particulate polymer has an initial particle size of from 0.5 mm to 7 mm.
5. The process according to claim 1 , wherein the mechanically pre-dried particulate polymer is comminuted after the mechanical pre-drying and before the end-drying.
6. The process according to claim 1 , wherein the particulate polymer has a particle size of from 0.5 mm to 7 mm after the end-drying.
7. The process according to claim 1 , wherein the particulate polymer is a polyethersulfone.
8. A process for working up particulate polymers, comprising:
i) dropletizing a polymer solution comprising a polymer and a first organic solvent (S 2 ) into a precipitation bath comprising a second organic solvent (S 3 ) and water to obtain a particulate polymer by precipitation,
ii) removing the precipitated particulate polymer from the precipitation bath,
iii) extracting residues of the first and/or second organic solvent from the particulate polymer with an extractant,
iv) drying the particulate polymer with the process according to claim 1 and
v) optionally finishing the particulate polymer.
9. The process according to claim 8 , wherein the first and/or second organic solvent is N-methylpyrrolidone.