Polycrystalline chemical vapour deposited diamond tool parts and methods of fabricating, mounting, and using the same
A polycrystalline CVD synthetic diamond work piece for use in a polycrystalline CVD synthetic diamond tool, the polycrystalline CVD synthetic diamond work piece comprising: a working surface; and a rear mounting surface; wherein an average lateral grain size of the rear mounting surface is no less than 10 μm, and wherein the working surface comprises: (a) smaller diamond grains than the rear mounting surface; (b) an average lateral grain size in a range 10 nm to 15 μm; and (c) a Raman signal generated by a laser focused on the working surface which exhibits one or more of the following characteristics: (1) an sp3 carbon peak at 1332 cm −1 having a full width half-maximum of no more than 8.0 cm −1 , (2) an sp2 carbon peak at 1550 cm −1 having a height which is no more than 20% of a height of an sp3 carbon peak at 1332 cm −1 after background subtraction when using a Raman excitation source at 633 nm; and (3) an sp3 carbon peak at 1332 cm −1 is no less than 10% of local background intensity in a Raman spectrum using a Raman excitation source at 785 nm.
1. A polycrystalline CVD synthetic diamond work piece for use in a polycrystalline CVD synthetic diamond tool, the polycrystalline CVD synthetic diamond work piece comprising:
a working surface;
and a rear mounting surface;
wherein an average lateral grain size of the rear mounting surface is no less than 10 μm, and
wherein the working surface comprises:
(a) smaller diamond grains than the rear mounting surface;
(b) an average lateral grain size in a range 10 nm to 15 μm; and
(c) a Raman signal generated by a laser focused on the working surface which exhibits both of the following characteristics:
(1) an sp3 carbon peak at 1332 cm −1 having a full width half-maximum of no more than 8.0 cm −1 ; and
(2) an sp2 carbon peak at 1550 cm −1 having a height which is no more than 20% of a height of an sp3 carbon peak at 1332 cm −1 after background subtraction when using a Raman excitation source at 633 nm.
2. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the average lateral grain size of the working surface is no less than 20 nm.
3. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the average lateral grain size of the working surface is no more than 12 μm.
4. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the average lateral grain size of the rear mounting surface is no less than 12 μm.
5. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the full width half-maximum of the sp3 carbon peak at 1332 cm −1 for the working surface is no more than 7.0 cm −1 .
6. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the sp2 carbon peak at 1550 cm −1 for the working surface is no more than 10% of the height of the sp3 carbon peak at 1332 cm −1 after background subtraction when using the Raman excitation source at 633 nm.
7. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein a thickness from the working surface to the rear mounting surface is no less than 200 μm.
8. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the working surface has at least one linear dimension of at least 6 mm.
9. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the polycrystalline CVD synthetic diamond work piece is in the form of: a wear part; a dresser; a wire drawing die; a gauge stone; or a cutter.
10. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the polycrystalline CVD synthetic diamond work piece comprises a cutting edge and the working surface extends from the cutting edge.
11. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the working surface has a surface flatness ≤5 μm.
12. A polycrystalline CVD synthetic diamond work piece according to claim 1 , wherein the working surface has a surface roughness R a ≤20 nm.
13. A polycrystalline CVD synthetic diamond tool comprising:
a polycrystalline CVD synthetic diamond work piece according to claim 1 ; and
a holder to which the polycrystalline CVD synthetic diamond work piece is mounted,
wherein the polycrystalline CVD synthetic diamond work piece is oriented such that the working surface of the polycrystalline CVD synthetic diamond work piece is exposed to form a working surface of the polycrystalline CVD synthetic diamond tool.
14. A method of processing a material using a polycrystalline CVD synthetic diamond tool according to claim 13 , the method comprising:
orienting the polycrystalline CVD synthetic diamond tool such that the working surface thereof is in contact with the material to be processed; and
processing the material by providing relative movement of the material and the working surface of the polycrystalline CVD synthetic diamond tool while the working surface of the polycrystalline CVD synthetic diamond tool is in contact with the material being processed.