Transparent organosilicon gel adhesive

1. A transparent organosilicon gel adhesive, characterized in that the transparent organosilicon gel adhesive is prepared by mixing component A with component B in accordance with the mass proportion of 1:1, wherein the component A is composed of materials of the following proportion by weight:

base material

60-95

parts by weight;

catalyst

0.1-0.5

part by weight;

auxiliary material

5-40

parts by weight;

wherein the catalyst is a platinum-group metal catalyst;

the component B is composed of materials of the following proportion by weight:

base material

60-95

parts by weight;

crosslinker

5-20

parts by weight;

inhibitor

0.1-0.5

part by weight;

auxiliary material

1-20

parts by weight;

wherein the base material is at least one of compounds conforming to general formula (1), compounds conforming to general formula (2), compounds conforming to general formula (3) and compounds conforming to general formula (4);

where R 1 represents alkyl with the number of carbon atoms of 1 to 6; R 2 , R 3 and R 4 represent alkyl with the number of carbon atoms of 1 to 6 or alkenyl with the number of carbon atoms of 2 to 8 respectively and independently; and x is equal to 5 to 40, and y is equal to 1 to 30;

where a is greater than or equal to 20, and b is greater than or equal to 30;

where c is greater than or equal to 20, d is greater than or equal to 30, and e is greater than or equal to 10;

where f is greater than or equal to 30, g is greater than or equal to 10, h is greater than or equal to 10, and i is greater than or equal to 10;

the crosslinker is at least one of compounds conforming to general formula (5);

where R 8 represents alkyl with the number of carbon atoms of 1 to 6; R 5 , R 6 and R 7 represent alkyl with the number of carbon atoms of 1 to 6 or hydroxyl respectively and independently, and at least one of R 5 , R 6 and R 7 is hydroxyl; and j is equal to 10 to 30, and k is equal to 1 to 10;

the auxiliary material contains MQ resin conforming to general formula (6) or a mixture of MQ resin conforming to general formula (6) and vinyl end silicone oil, wherein the mass proportion of the MQ resin to the vinyl end silicone oil is 0.3 to 0.4:0.6 to 0.7;

the auxiliary material also contains MT resin or a mixture of MT resin and vinyl end silicone oil, wherein the mass proportion of the MT resin to the vinyl end silicone oil is 0.3 to 0.4:0.6 to 0.7;

(Me 3 SiO 0.5 ) l (R 9 Me 2 SiO 0.5 ) m (SiO 2 )  (6);

where Me represents methyl; R 9 represents alkyl, cyclopropyl, cyclobutyl, cyclopentyl or cyclohexyl with the number of carbon atoms of 1 to 6 or alkenyl with the number of carbon atoms of 2 to 7; and l is equal to 0 to 1.5, m is equal to 0 to 1.5, and l+m is equal to 1.3 to 1.8;

the auxiliary material also contains an adhesion promoter, wherein the adhesion promoter is prepared by mixing component C and component D, wherein the mass proportion of the component C to the component D is 10 to 90:10 to 90; the component C is at least one of compounds conforming to general formula (7), compounds conforming to general formula (8), compounds conforming to general formula (9) and compounds conforming to general formula (10); the component D is at least one of compounds conforming to general formula (11);

where q is equal to 3 to 6, r is equal to 2 to 6, s is equal to 6 to 12, t is equal to 2 to 6, u is equal to 3 to 6, v is equal to 6 to 12, and w is equal to 1 to 12;

the inhibitor is at least one of alkynol compounds and alkenyl-containing cyclic siloxane oligomers.

2. The transparent organosilicon gel adhesive of claim 1 , characterized in that the platinum-group metal catalyst is one of chloroplatinic acid, alcohol-modified chloroplatinic acid, platinum-vinyl siloxane composition, chloroplatinic acid-alkene complex and platinum-alkene composition.

3. The transparent organosilicon gel adhesive of claim 2 , characterized in that the platinum-group metal catalyst is platinum-vinyl siloxane composition.

4. The transparent organosilicon gel adhesive of claim 1 , characterized in that the inhibitor is selected from 3-methyl-1-butyn-3-ol, 3-methyl-1-pentyn-3-ol, 3,5-dimethyl-1-hexyn-3-ol, 1-hexynyl-1-cyclohexanol, 3-phenyl-1-butyn-3-ol, 2-methyl-3-butyn-2-ol, tetravinyl tetramethylcyclo tetrasiloxane, pyridine and unsaturated acylamide.

5. The transparent organosilicon gel adhesive of claim 1 , characterized in that the alkenyl group in the compound conforming to general formula (1) is selected from the group consisting of vinyl, allyl, butenyl, pentenyl, hexenyl or heptenyl.

6. The transparent organosilicon gel adhesive of claim 1 , characterized in that R 1 and R 2 in the compound conforming to general formula (1) represent methyl, and R 3 and R 4 represent vinyl, wherein the content of vinyl is 0.005-0.5 wt %; and the viscosity of the compound conforming to general formula (1) is 300-30,000 cP;

alternatively, R 1 in the compound conforming to general formula (1) represents methyl, and R 2 , R 3 and R 4 represent vinyl, wherein the content of vinyl is 0.01-10 wt %; and the viscosity of the compound conforming to general formula (1) is 50-10,000 cP;

alternatively, R 1 , R 2 and R 3 in the compound conforming to general formula (1) represent methyl, and R 4 represent vinyl, wherein the content of vinyl is 0.001-0.5 wt %; and the viscosity of the compound conforming to general formula (1) is 500-10,000 cP.

7. The transparent organosilicon gel adhesive of claim 1 , characterized in that R 5 and R 8 in the compound conforming to general formula (5) represent methyl, and R 6 and R 7 represent hydroxyl, wherein the content of hydrogen contained in the compound conforming to general formula (5) is 0.005-1 wt %; and the viscosity of the compound conforming to general formula (5) is 5-200 cP;

alternatively, R 6 , R 7 and R 8 in the compound conforming to general formula (5) represent methyl, and R 5 represents hydroxyl, wherein the content of hydrogen contained in the compound conforming to general formula (5) is 0.005-2 wt %; and the viscosity of the compound conforming to general formula (5) is 10-100 cP;

alternatively, R 8 in the compound conforming to general formula (5) represents methyl, and R 5 , R 6 and R 7 represent hydroxyl, wherein the content of hydrogen contained in the compound conforming to general formula (5) is 0.001-10 wt %; and the viscosity of the compound conforming to general formula (5) is 10-300 cP.

8. The transparent organosilicon gel adhesive of claim 1 , characterized in that in the MQ resin, R 9 represents methyl, wherein the ratio of M to Q of the MQ resin is 0.6 to 1.2;

alternatively, in the MQ resin, R 9 represents vinyl, wherein the content of vinyl is less than or equal to 10 wt %.

9. The transparent organosilicon gel adhesive of claim 8 , characterized in that the ratio of M to Q of the MQ resin is 0.8.