Barrier coat for open tool molding
View Patent ↗A multilayer composite contains a gel coat layer, a laminate layer, and a barrier layer disposed between the gel coat and the laminate layer. The laminate contains from 40–80% by weight paste and from 20–60% by weight reinforcing fibers. The barrier coat also comprises a cured polyester resin, and contains reinforcing fibers shorter than those in the laminate layer. The barrier layer has sufficient flexibility to avoid cracking during demolding and handling. Preferably, the barrier layer exhibits an elongation at break of more than 1%, and more preferably about 2% or more. The resin of the barrier layer can contain up to about 25% by weight of the resin of an isophthalic acid based polyester resin. The composites can be made using an open tool molding process.
1. A multilayer composite article comprising:
a gel coat layer comprising a thermosetting resin;
a fiber reinforced laminate layer comprising a first set of fibers having a first length; and
a barrier layer disposed between the gel coat layer and the laminate layer;
wherein the barrier layer comprises a second set of fibers dispersed in a polyester resin, said second fibers having a second length shorter than the first length wherein the first length is 6 mm or greater and the second length is 1 mm or less.
2. A multilayer composite according to claim 1 , wherein the polyester resin comprises up to 25% of an isophthalic acid resin, based on the total weight of the polyester resin.
3. A multilayer composite according to claim 1 , wherein the polyester resin comprises 75–100% by weight of a dicyclopentadiene resin, based on the total weight of the polyester resin.
4. A multilayer composite according to claim 1 , wherein the polyester resin comprises 75–99% by weight dicyclopentadiene resin and 1–25% by weight isophthalic resin.
5. A multilayer composite according to claim 1 , wherein the second length is 0.5 mm or less.
6. A multilayer composite according to claim 1 , wherein the second length is 0.4 mm or less.
7. A multilayer composite according to claim 1 , wherein the gel coat is ½–2 mm thick, the barrier coat is 1–3 mm thick, and the laminate layer is 2–5 mm thick.
8. A multilayer composite according to claim 1 , wherein the barrier coat comprises up to 45% by weight milled glass fibers of length less than 1 mm and 50–95% by weight resin comprising dicyclopentadiene resin and isophthalic acid ratio in a ratio of at least 4:1.
9. A multilayer composite according to claim 1 , wherein the barrier coat further comprises polymeric hollow microspheres.
10. An automotive body panel comprising:
a gel coat layer;
a laminate layer; and
a barrier coat disposed between the gel coat and the laminate layer,
wherein the barrier coat comprises a polyester resin and reinforcing fibers of length 1 mm or less.
11. A body panel according to claim 10 , wherein the barrier coat exhibits an elongation at break of at least 1%.
12. A body panel according to claim 10 , wherein the barrier coat exhibits an elongation at break of at least 2%.
13. A body panel according to claim 10 , wherein the barrier coat comprises dicyclopentadiene resin and isophthalic resin in a ratio of 4:1 and higher.
14. A body panel according to claim 10 , wherein the laminate layer comprises a dicyclopentadiene resin and glass fibers of 6 mm in length or greater.
15. A body panel according to claim 14 , wherein the laminate further comprises hollow polymeric microspheres.
16. A body panel according to claim 10 , wherein the laminate layer, the barrier coat, or both further comprise a pigment.
17. A body panel according to claim 16 , wherein the pigment comprises carbon black.
18. A body panel according to claim 10 , wherein the barrier coat comprises reinforcing glass fibers of length 0.5 mm or less.
19. A barrier coat composition comprising:
a resin component comprising:
80–100 parts of dicyclopentadiene resin and up to 20 parts of an isophthalic acid resin, and
a reinforcing fiber component comprising fibers having a length of 1 mm or less mixed with the resin component.
20. A composition according to claim 19 , wherein the reinforcing fiber component comprises fibers having a length of 0.5 mm or less.
21. A composition according to claim 19 , wherein the fibers have a length of about 0.4 mm.
22. A composition according to claim 19 , wherein the fibers have a length of about 0.025 mm.
23. A composition according to claim 19 , wherein the composition exhibits an elongation at break of 1% or greater.
24. A composition according to claim 19 , wherein the composition exhibits an elongation at break of 2% or greater.
25. A composition according to claim 19 , wherein the barrier coat further comprises a filler selected from the group consisting of hollow glass microspheres and polymeric hollow microspheres.
26. A composition according to claim 19 , wherein the resin comprises up to 40% by weight styrene monomer.
27. A method for preparing a composite article by spray up operation, comprising the steps of:
applying a gel coat into a mold;
applying a barrier coat over the gel coat in the mold; and
applying a laminate formula over the barrier coat,
wherein applying the laminate formula comprises providing the laminate formula comprising 20–60% by weight of first reinforcing fibers having a first length of 6 mm or greater and 40–80% by weight of a paste comprising a laminate coat polyester resin; and
wherein applying the barrier coat comprises providing second fibers having a length of 1 mm or less dispersed in a barrier coat polyester resin.
28. A method according to claim 27 , wherein the gel coat applied to a thickness of 0.2 to 2 mm, the barrier coat is applied to a thickness of 0.5 to 5 mm, and the laminate layer is applied to a thickness of 1–10 mm.
29. A method according to claim 27 , wherein the thickness of the composite article is from 2 to 15 mm.
30. A method according to claim 27 , wherein the composite article is an automotive body panel.
31. A method according to claim 27 , wherein the laminate formula fiber comprises polymeric hollow microspheres.
32. A method according to claim 27 , wherein the first reinforcing fiber comprise glass fibers of 12 mm or greater in length.
33. A method according to claim 27 , wherein the barrier coat polyester resin comprises 75–100 parts of a dicyclopentadiene resin and 1–25 parts of an isophthalic acid resin.
34. A method of producing an automotive body panel comprising the steps of:
applying a gel coat composition to a mold surface;
applying a barrier coat composition to the gel coat in the mold;
applying a fiber reinforced laminate composition comprising fibers having a first length onto the barrier coat in the mold;
curing at 50° C. or less; and
removing the cured article from the mold,
wherein applying the barrier coat comprises providing glass fibers having length of 1 mm or less dispersed in a polyester resin.
35. A method according to claim 34 , wherein the gel coat comprises a thermosetting resin.
36. A method according to claim 34 , wherein the barrier coat exhibits elongation at break of 1% or greater.
37. A method according to claim 34 , wherein the barrier coat exhibits elongation at break of 2% or greater.
38. A method according to claim 34 , wherein the barrier coat comprises 100 parts of a polyester, including up to 20 parts of an isophthalic acid polyester resin.
39. A method according to claim 38 , wherein the barrier coat comprises a dicyclopentadiene resin.
40. A method according to claim 39 , wherein the barrier coat comprises glass fibers having a length of 1 mm or less.
41. A method according to claim 34 , wherein the barrier coat comprises glass fibers having a length of 0.5 mm or less.
42. A method according to claim 34 , comprising the steps of applying the gel coat to a thickness of 0.5–2 mm, applying the barrier coat to a thickness of 1–3 mm, and applying the laminate coat to a thickness of 2–5 mm.