Methods for removing moisture from hydrogen halides
View Patent ↗A composition comprising a magnesium halide coated macroporous carbonaceous substrate is provided for effecting moisture removal from a hydrogen halide fluid. Moisture removal is effected by intimately contacting the hydrogen halide fluid with the magnesium halide coated macroporous carbonaceous substrate and separating the fluid from the coated substrate.
1. A method of removing water from gaseous HCl by passing the HCl stream containing water over an adsorbent of anhydrous MgCl 2 supported on an activated carbonaceous substrate that is liquid hydrogen halide tolerant.
2. The method of claim 1 including the step of activating the adsorbent by heating the adsorbent prior to passing the HCl stream containing water over said adsorbent.
3. The method of claim 2 wherein the adsorbent is heated to a temperature of about 240° C.
4. The method of claim 1 wherein the concentration of MgCl 2 is at least about 0.1 moles of MgC 2 per liter of substrate.
5. The method of claim 1 wherein the concentration of MgCl 2 is at least about 1.2 moles of MgCl 2 per liter of substrate.
6. The method of claim 1 wherein at least about 1.8% by weight MgCl 2 is present on the substrate.
7. The method of claim 1 wherein at least about 17.7% by weight MgCl 2 is present on the substrate.
8. The method of claim 1 wherein the HCl stream contains about 4 ppm water.
9. The method of claim 1 wherein the substrate is macroporous.
10. The method of claim 1 wherein the resultant HCl contains less than about 100 ppb water.
11. A method of removing water from HCl by passing the HCl stream containing water over an adsorbent of anhydrous magnesium chloride supported on an activated carbonaceous support that is liquid hydrogen halide tolerant; wherein the anhydrous magnesium chloride supported on the activated carbonaceous substrate is produced by depositing a solution of dialkyl magnesium in an amount sufficient to coat the surface and fill the void volume of the porous carbonaceous substrate; and contacting the substrate with hydrogen chloride to convert the dialkyl magnesium to magnesium chloride.
12. The method of claim 11 including the step of activating the adsorbent by heating the adsorbent prior to passing said HCl stream containing water over said adsorbent.
13. The method of claim 12 wherein the adsorbent is heated to a temperature of about 240° C.
14. The method of claim 11 wherein the concentration of magnesium chloride is at least about 0.1 moles of magnesium chloride per liter of carbonaceous support.
15. The method of claim 11 wherein the concentration of magnesium chloride is at least about 1.2 moles of magnesium chloride per liter of carbonaceous support.
16. The method of claim 11 wherein the support is macroporous.
17. A method of removing water from a hydrogen halide fluid by passing the hydrogen halide stream containing water over an adsorbent of anhydrous magnesium halide supported on a carbonaceous substrate that is liquid hydrogen halide tolerant, wherein said carbonaceous substrate does not react with said hydrogen halide to produce products which contaminate the hydrogen halide.
18. The method of claim 17 wherein said carbonaceous substrate does not react with said hydrogen halide to produce particulate products which contaminate the dehydrated hydrogen halide.
19. The method of claim 17 wherein said substrate is an activated carbonaceous support.
20. The method of claim 19 wherein said substrate is macroporous.
21. The method of claim 17 wherein said substrate is macroporous.
22. The method of claim 17 wherein said hydrogen halide is hydrogen chloride and said magnesium halide is magnesium chloride.
23. The method of claim 17 wherein said hydrogen halide is hydrogen bromide and said magnesium halide is magnesium bromide.
24. A method of removing water from a hydrogen halide fluid by passing the hydrogen halide stream containing water over an adsorbent of anhydrous magnesium halide supported on a carbonaceous substrate at pressures of about 1100 psig at 50° C., thereby producing dehydrated hydrogen halide, wherein said carbonaceous substrate is liquid hydrogen halide tolerant and does not react with said hydrogen halide to produce products which contaminate the dehydrated hydrogen halide and; wherein the magnesium halide supported on the activated carbonaceous substrate is produced by depositing a solution of dialkyl magnesium in an amount sufficient to coat the surface and fill the void volume of the porous carbonaceous substrate; and contacting the substrate with hydrogen halide to convert the dialkyl magnesium to magnesium halide.
25. A method of removing water from liquid HCl by passing the HCl stream containing water over an adsorbent of anhydrous MgCl 2 supported on an activated carbonaceous substrate that is liquid hydrogen halide tolerant.