Lithium-containing complex oxide and method of producing same
View Patent ↗A lithium-containing complex oxide exhibits a high performance as a cathode active material of a lithium secondary cell or the like and having a high tap density. A granular lithium-containing complex oxide, such as lithium manganese complex oxide, is made up of “complex oxide grains produced by integrating lithium-rich material grains abnormally grown during a firing reaction with the surfaces of the base grains by sintering.” The number of complex oxide grains is not more than 50 per gram of the complex grains. A metal oxide such as manganese oxide and lithium carbonate not more than 5 μm in average grain size are mixed by means of a mixer which grinds and mixes particles by using a shearing force and heated and fired at a warming rate of not more than 50° C./h., thus producing the lithium-containing complex oxide.
1. A lithium-containing complex oxide comprising spherical complex oxide grains having a tap density of not less than 1.8 g/cm 3 produced by causing lithium-rich material grains to be sintered and integrated with the respective surfaces of base grains, wherein the number of the complex oxide grains comprising the lithium-rich material grains that have abnormally grown during a firing reaction to be sintered and integrated with the respective surfaces of the base grains is at a ratio not more than 50 pieces per gram of the complex oxide grains.
2. The lithium-containing complex oxide according to claim 1 , wherein the lithium-containing complex oxide is a lithium-manganese complex oxide.
3. A method of producing a lithium-containing complex oxide by mixing a metal oxide with lithium carbonate, as raw materials, to be sintered together, said method comprising the steps of mixing the raw materials by means of a mixer for grinding and mixing by a shearing force and executing sintering at a warming rate of not more than 50° C./h in which lithium carbonate not more than 5 μm in average grain size is used, thereby obtaining the lithium-containing complex oxide of claim 1 .
4. The method of producing a lithium-containing complex oxide according to claim 3 , wherein the metal oxide as the raw material for sintering is a manganese oxide.
5. The method of producing a lithium-containing complex oxide according to claim 4 , wherein the manganese oxide as the raw material for sintering is a manganese oxide composed of fine grains not more than 10 μm in median grain size.
6. The method of producing a lithium-containing complex oxide according to claim 3 , wherein the mixer is a rotary blade mixer.