Metalothermic reduction of refractory metal oxides
View Patent ↗A method of producing a refractory metal powder by (A) combining (i) an oxide particle component and (ii) a reducing agent; (B) forming a substantially uniform mixture of (i) and (ii); (C) continuously feeding the mixture into a furnace; (D) igniting the mixture at a reaction zone and starting a reaction that is sufficiently exothermic to form a high temperature flash; (E) starting a reaction that is sufficiently exothermic to form a high temperature self-sustaining flash; and (F) producing a free-flowing reduced oxide powder.
1. A method of producing a refractory metal powder comprising:
(A) blending (i) an oxide particle component which contains a refractory metal and said refractory metal is tantalum or niobium and (ii) a solid reducing agent;
(B) forming a substantially uniform mixture of (i) and (ii);
(C) continuously feeding the mixture into a furnace;
(D) igniting the mixture at a reaction zone and staffing a reaction that is form a high temperature exothermic to form a high temperature flash;
(E) starting a reaction that is sufficiently exothermic to form a high temperature self-sustaining flash; and
(F) producing a free-flowing reduced oxide powder and wherein the furnace has a cross-sectional area and the mixture formed in (B) is fed in to the furnace in (C) by a dispersing means excluding a rotor/stator disperser, such that it is uniformly distributed across the cross-sectional area of the furnace and the residence time of the mixture in the reaction zone is from 0.1 second to 10 seconds.
2. The method according to claim 1 , wherein the oxide particle component (i) is free-flowing.
3. The method according to claim 1 , wherein the reducing agent component (ii) is free-flowing.
4. The method according to claim 1 , wherein the mixture formed in (B) is free-flowing.
5. The method according to claim 1 , wherein the flash formed in (D) is self sustaining.
6. The method according to claim 1 , wherein the oxide particles in (i) are selected from the group consisting of metal oxide particles, metal alloy oxide particles, refractory metal suboxide powders, refractory metal alloy suboxide powders and mixtures thereof.
7. The method according to claim 1 , wherein the reducing agent (ii) is selected from the group consisting of magnesium, aluminum, calcium and mixtures thereof.
8. The method according to claim 1 , wherein the reduced oxide powder is selected from the group consisting of refractory metal powders, refractory metal alloy powders, refractory metal suboxide powders, refractory metal alloy suboxide powders and mixtures thereof.
9. The method according to claim 1 , wherein the dispersing means is selected from the group consisting of a horizontal screen disperser, an impact de-agglomerator, a rotating disc disperser, a blender and a mixer.
10. The method according to claim 1 , wherein the furnace has a first temperature at a location that is not the reaction zone and the flash is at a second temperature that is greater than the first temperature.
11. The method according to claim 10 , wherein the mixture is introduced at a consistently constant rate and the second temperature remains substantially constant.
12. The method according to claim 1 , wherein said oxide component contains a refractory metal oxide or a refractory alloy metal oxide and the flash has a temperature that is less than or equal to the melting point of the refractory metal oxide or refractory alloy metal oxide.
13. The method according to claim 1 , wherein the particles in the mixture have a particle size distribution of less than 600 μm as determined by laser light scattering.
14. The method according to claim 1 , wherein the reaction zone has a length from 0.1 m to 15 m in length.
15. The method according to claim 1 , wherein the bulk density of the mixture is from 0.05 to 6 g/cm 3 .
16. The method according to claim 1 , wherein the furnace is a vertical tube furnace.
17. The method according to claim 1 , further comprising forming the powder into pellets at an appropriate sintering temperature.
18. The method according to claim 17 , further comprising forming the sintered pellets into electrolytic capacitors.
19. The method according to claim 1 , wherein the method is continuous.
20. A method of producing a refractory metal powder comprising:
(A) blending (i) an oxide particle mixture containing oxide particles selected from the group consisting of refractory metal oxide particles, refractory metal alloy oxide particles, refractory metal suboxide powders, refractory metal alloy suboxide powders and mixtures thereof and said refractory metal is tantalum or niobium and (ii) a solid reducing agent selected from the group consisting of magnesium, aluminum, calcium and mixtures thereof;
(B) forming a substantially uniform mixture of (i) and (ii);
(C) continuously feeding the mixture into a furnace;
(D) igniting the mixture at a reaction zone and starting a reaction that is sufficiently exothermic to form a high temperature flash; and
(E) producing a free-flowing reduced oxide powder group consisting of refractory metal powders, refractory metal alloy thereof;
wherein the mixture is introduced at a consistently constant rate and has a second temperature and the second temperature remains substantially constant,
and wherein the furnace has a cross-sectional area and the mixture formed in (B) is fed in to the furnace in (C) by a dispersing means excluding a rotor/stator disperser, such that it is uniformly distributed across the cross-sectional area of the furnace and the residence time of the mixture in the reaction zone is from 0.1 second to 10 seconds.
21. The method according to claim 20 , wherein the oxide particle component (i) is free-flowing.
22. The method according to claim 20 , wherein the reducing agent component (ii) is free-flowing.
23. The method according to claim 20 , wherein the mixture formed in (B) is free-flowing.
24. The method according to claim 20 , wherein the flash formed in (D) is self-sustaining.
25. The method according to of claim 20 , wherein the furnace is a vertical tube furnace.
26. The method according to claim 20 , wherein the method is continuous.
27. A method of producing a refractory metal powder comprising:
(A) blending (i) an oxide particle mixture containing oxide particles selected from the group consisting of refractory metal oxide particles, refractory metal alloy oxide particles, refractory metal suboxide powders, refractory metal alloy suboxide powders and mixtures thereof and said refractory metal is tantalum or niobium and (ii) a solid reducing agent selected from the group consisting of magnesium, aluminum, calcium and mixtures thereof;
(B) forming a substantially uniform mixture of (i) and (ii);
(C) reducing the free-flowing mixture in a reaction zone by heating the mixture in a reaction vessel to create a highly exothermic reaction, the exothermic reaction being triggered by heating the mixture to an ignition temperature or by adding a further reagent or catalyst; and
(D) recovering a high surface area powder, substantially free of impurities, which is selected from the group consisting of refractory metal powders, refractory metal alloy powders, refractory metal suboxide powders and refractory metal alloy suboxide powders and
wherein the reaction vessel has a cross-sectional area and the mixture formed in (B) is fed in to the reaction vessel in (C) by a dispersing means excluding a rotor/stator disperser, such that it is uniformly distributed across the cross-sectional area of the reaction vessel and the residence time of the mixture in the reaction zone is from 0.1 second to 10 seconds.
28. The method according to claim 27 , wherein the oxide particle component (i) is free-flowing.
29. The method according to claim 27 , wherein the reducing agent component (ii) is free-flowing.
30. The method according to claim 27 , wherein the mixture formed in (B) is free-flowing.
31. The method according to claim 27 , wherein the reaction in (C) is self-sustaining.
32. The method according to claim 27 , wherein the reaction vessel is a vertical tube furnace.
33. The method according to claim 27 , wherein the refractory metal oxide component is selected from the group consisting of tantalum pentoxide, niobium pentoxide, niobium suboxide, tungsten trioxide, chromium trioxide, molybdenum trioxide, titanium dioxide, vanadium pentoxide and niobium oxide, mixtures of at least one of the foregoing and zirconium dioxide, and mixtures thereof.
34. The method according to claim 27 , wherein the refractory metal powder and the refractory metal alloy powder are selected from the group consisting of tantalum, niobium, molybdenum, tungsten, vanadium, chromium, titanium and combinations thereof.
35. The method according to claim 27 , wherein the temperature in the reaction zone is less than or equal to the melting point of the refractory metal feed.
36. The method according to claim 27 , wherein the powder further comprises agglomerates having a substantially uniform particle size distribution.
37. The method according to claim 27 , further comprising adjusting at least one process parameter to control the chemical and physical properties of the powder, wherein the process parameter is selected from the group consisting of reagent feed rates, ignition temperature, steady state energy supply, reagent particle size, reducing agent stoichiometry and inert carrier gas flow rate.
38. The method according to claim 27 , wherein the reducing agent in the mixture is provided in an amount substantially equal to the stoichiometric quantity required to react with the refractory metal oxide component.
39. The method according to claim 27 , further comprising forming the powder into pellets at an appropriate sintering temperature.
40. The method according to claim 39 , further comprising forming the sintered pellets into electrolytic capacitors.
41. The method according to claim 27 , wherein the recovering step (D) further comprises agglomerating and/or deoxidizing.
42. The method according to claim 27 , wherein the method is continuous.