Granted Patent B2

US 7,431,751 · App. 10/953,163 · Granted Oct 7, 2008

Abstract

Claims (36)

1. A method of producing a refractory metal powder comprising:

(A) heating a mixture comprising a metal oxide powder and magnesium at a flash temperature to produce a metal powder containing magnesium tantalate or magnesium niobate wherein said magnesium in the mixture is in an amount substantially equal to the stoichiometric quantity required to react with the metal oxide, and said flash temperature is near but less than the melting point of the metal oxide; and

(B) heating the powder in an inert atmosphere in the presence of a reducing agent to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder (reduction step) and heating the powder under vacuum to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder (heating under vacuum step), the reduction step and heating under vacuum step can be performed in any order.

2. The method according to claim 1 , wherein the metal powder is tantalum or niobium and is free-flowing.

3. The method according to claim 1 , wherein the reducing agent in step (B) is selected from the group consisting of magnesium, aluminum, calcium, and combinations thereof.

4. The method according to claim 1 , wherein the temperature in (B) is a temperature at which the magnesium tantalate or magnesium niobate is unstable.

5. The method according to claim 1 , wherein the reduction step in (B) is conducted in the presence of an inert gas.

6. The method according to claim 5 , wherein the inert gas is selected from neon and argon.

7. The method according to claim 1 , wherein the temperature in the reduction step in (B) is from 800° C. to 1,300° C.

8. The method according to claim 1 , wherein the temperature in the heating under vacuum step in (B) is from 1,100° C. to 1,400° C.

9. The method according to claim 1 , wherein the temperature in the reduction step in (B) is from 875° C. to 925° C. for from 2 to 4 hours.

10. The method according to claim 1 , wherein the reduction step in (B) is carried out by heating the powder under vacuum at 1,100° C. to 1,400° C. for from 15 minutes to 6 hours.

11. The method according to claim 1 , wherein step (B) is carried out by

I) heating the metal powder under vacuum at 1,100° C. to 1,400° C. for from 15 minutes to 6 hours, and

ii) heating the powder in the presence of a reducing agent at 800° C. to 1,300° C. for from 1 to 6 hours.

12. The method according to claim 11 , wherein the heating step (ii) is conducted in the presence of an inert gas.

13. The method according to claim 12 , wherein the inert gas is selected from neon and argon.

14. The method according to claim 1 , wherein step (B) is carried out by

I) heating the powder in the presence of a reducing agent at 800° C. to 1,300° C. for from 1 to 6 hours; and

ii) heating the metal powder under vacuum at 1,100° C. to 1,400° C. for from 15 minutes to 6 hours.

15. The method according to claim 14 , wherein the heating step (i) is conducted in the presence of an inert gas.

16. The method according to claim 15 , wherein the inert gas is selected from neon and argon.

17. The method according to claim 1 , wherein the magnesium tantalate and/or magnesium niobate in (A) are present at from 0.02 wt. % to 7 wt. % based on the weight of the metal powder.

18. The method according to claim 1 , wherein after step (B), the magnesium tantalate and/or magnesium niobate are present at less than 500 ppm.

19. The method according to claim 1 , further comprising forming the refractory metal powder into pellets at an appropriate sintering temperature.

20. The method according to claim 19 , further comprising forming the sintered pellets into electrolytic capacitors.

21. The method as claimed in claim 1 , wherein the reducing agent is present in an amount from 1% to 2% based on the weight of the metal powder.

22. A method of producing a refractory metal powder comprising:

(A) heating a mixture comprising a metal oxide powder and magnesium at a flash temperature to produce a metal powder containing magnesium tantalate or magnesium niobate wherein said magnesium in the mixture is in an amount substantially equal to the stoichiometric quantity required to react with the metal oxide, and said flash temperature is near but less than the melting point of the metal oxide; and

(B) heating the powder under vacuum to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder.

23. A method of producing a refractory metal powder comprising:

(A) heating a mixture comprising a metal oxide powder and magnesium at a flash temperature to produce a metal powder containing magnesium tantalate or magnesium niobate wherein said magnesium in the mixture is in an amount substantially equal to the stoichiometric quantity required to react with the metal oxide, and said flash temperature is near but less than the melting point of the metal oxide; and

(B) heating the powder in an inert atmosphere in the presence of a reducing agent at a temperature from 875°C. to 1,300° C. in order to remove magnesium tantalate or magnesium niobate from the powder (reduction step) and/or heating the powder under vacuum to a temperature sufficient to remove magnesium tantalate or magnesium niobate from the powder (heating under vacuum step), the reduction step and heating under vacuum step can be performed in any order.

24. The method as claimed in claim 23 , wherein the temperature in the reduction step is from 875°C. to 925°C.

25. The method as claimed in claim 24 , wherein the reducing agent is present in an amount from 1% to 2% based on the weight of the metal powder.

26. The method as claimed in claim 23 , wherein the reducing agent is present in an amount from 0.1% to 5% based on the weight of the metal powder.

Assignments (12)