Copper alloy and method of manufacturing the same
View Patent ↗A copper alloy of superior flex durability is provided that is suitable for the conducting members of flexible printed circuits. This is a copper alloy where the integrated intensity ratio I {200} /I {111} found by x-ray diffraction of the rolled surface is 1.5 or less. Examples of its specific chemical composition are: a composition where, in percent by weight, Fe: 0.045-0.095%, P: 0.010-0.030%, the sum of all elements other than Fe, P and Cu is less than 1% and the balance is Cu, and a composition where, in percent by weight, Ni: 0.5-3.0%,Sn: 0.5-2.0%, P: 0.03-0.10%, the sum of all elements other than Ni, Sn, P and Cu is less than 1% and the balance is Cu. The copper alloy has a conductivity of 85% IACS or greater.
1. A copper alloy foil having a thickness of 16 μm or less, wherein an integrated intensity ratio I {200} /I {111} found by x-ray diffraction of a rolled surface is 1.5 or less, the copper alloy foil has a chemical composition, in percent by weight, of Fe: 0.045-0.095%, P: 0.010-0.030%, wherein Fe/P mass ratio is 3 to 3.8, the sum of all elements other than Fe, P and Cu is less than 1% and the balance is Cu, and the copper alloy foil exhibits a deformation texture wherein Fe—P based precipitates are present in a Cu matrix.
2. The copper alloy foil according to claim 1 , wherein, when test pieces are obtained in the longitudinal direction (LD) and transverse direction (TD) with respect to the direction of rolling and a MIT folding endurance test based on ASTM D-2176 is performed under the conditions of: bending angle: ±135°, load: 500 g, bending radius: 0.8 mm, the MIT folding endurance is 800 or more cycles in both the LD and TD.
3. The copper alloy foil according to claim 1 , wherein, when test pieces are obtained in the longitudinal direction (LD) and transverse direction (TD) with respect to the direction of rolling and a MIT folding endurance test based on ASTM D-2176 is performed under the conditions of: bending angle: ±135°, load: 500 g, bending radius: 0.8 mm, the MIT folding endurance is 1500 or more cycles in both the LD and TD.
4. The copper alloy foil according to claim 1 , wherein after being subjected to a heating test for one hour at 300° C. in a nitrogen atmosphere, the copper alloy has a tensile strength of 300 N/mm 2 or greater in both the longitudinal direction (LD) and the transverse direction (TD) with respect to the direction of rolling.
5. The copper alloy foil according to claim 1 , wherein the copper alloy has a conductivity of 85% IACS or greater.
6. A copper alloy foil having a thickness of 25 μm or less, wherein an integrated intensity ratio I {200} /I {111} found by x-ray diffraction of a rolled surface is 1.5 or less, the copper alloy foil has a chemical composition, in percent by weight, of Ni: 0.5-3.0%, Sn: 0.5-2.0%, P: 0.03-0.10%, the sum of all elements other than Ni, Sn, P and Cu is less than 1% and the balance is Cu, and the copper alloy foil exhibits a deformation texture wherein Ni-P based precipitates are present in a Cu matrix.
7. The copper alloy foil according to claim 6 , wherein, when test pieces are obtained in the longitudinal direction (LD) and transverse direction (TD) with respect to the direction of rolling and a MIT folding endurance test based on ASTM D-2176 is performed under the conditions of: bending angle: ±135°, load: 500 g, bending radius: 0.8 mm, the MIT folding endurance is 800 or more cycles in both the LD and TD.
8. The copper alloy foil according to claim 6 , wherein, when test pieces are obtained in the longitudinal direction (LD) and transverse direction (TD) with respect to the direction of rolling and a MIT folding endurance test based on ASTM D-2176 is performed under the conditions of: bending angle: ±135°, load: 500 g, bending radius: 0.8 mm, the MIT folding endurance is 1500 or more cycles in both the LD and TD.
9. The copper alloy foil according to claim 6 , wherein after being subjected to a heating test for one hour at 300° C. in a nitrogen atmosphere, the copper alloy has a tensile strength of 300 N/mm 2 or greater in both the longitudinal direction (LD) and the transverse direction (TD) with respect to the direction of rolling.
10. The copper alloy foil according to claim 6 , wherein the copper alloy has a conductivity of 85% IACS or greater.