Methods of making molybdenum titanium sputtering plates and targets
View Patent ↗Molybdenum titanium sputter targets are provided. In one aspect, the targets are substantially free of the β(Ti, Mo) alloy phase. In another aspect, the targets are substantially comprised of single phase β(Ti, Mo) alloy. In both aspects, particulate emission during sputtering is reduced. Methods of preparing the targets, methods of bonding targets together to produce large area sputter targets, and films produced by the targets, are also provided.
1. A method for preparing a molybdenum-titanium sputtering target having substantially no β(Ti, Mo) phase present comprising:
(a) providing powders of molybdenum and titanium wherein said titanium powder is present in an amount of 40-95 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder;
(b) blending the molybdenum and titanium powders to produce a blended powder;
(c) optionally, consolidating the blended powder;
(d) encapsulating the consolidated powder; and
(e) compacting while heating the encapsulated powder at 700° C. to 950° C. at a pressure from 75 to 175 MPa, to produce a first MoTi target plate.
2. The method of claim 1 , wherein in step (e) the compacting is performed at a pressure of 100 to 175 MPa and the heating is carried out at a temperature of 725°-925° C. for a period of 2-16 hours.
3. The method of claim 1 , wherein the molybdenum powder has an average particle size of 20 microns or less.
4. The method of claim 1 , wherein the titanium powder has an average particle size of 40 to 150 microns.
5. The method of claim 1 , wherein the consolidating of step (c) is performed in a cold isostatic press.
6. The method of claim 1 , wherein the compacting/heating of step (e) is performed in a hot isostatic press.
7. The method of claim 1 , further comprising the steps of:
(f) removing a portion of the encapsulation on the first target plate;
(g) bonding the first target plate to a second MoTi target plate along an edge of the first and second plates to produce bonded plates;
and
(h) compacting while heating the bonded plates to produce a bonded target plate.
8. The method of claim 7 , wherein the bonded target plate is at least 55 inches by 67 inches in area.
9. The method of claim 7 , wherein the compacting and heating of step (h) is hot isostatic pressing carried out at a pressure of 75-175 MPa and a temperature of 750°-850° C.
10. The method of claim 1 , wherein said titanium powder is present in an amount of 40-60 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder.
11. The method of claim 1 , wherein said titanium powder is present in an amount of 50-60 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder.
12. A method for preparing a molybdenum-titanium sputtering target having substantially no β(Ti, Mo) phase present comprising:
(a) providing powders of molybdenum and titanium wherein said titanium powder is present in an amount of 40-95 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder;
(b) blending the molybdenum and titanium powders to produce a blended powder;
(c) consolidating the blended powder;
(d) encapsulating the consolidated powder; and
(e) compacting while heating under pressure the encapsulated powder to produce a first MoTi target plate.
13. The method of claim 12 , wherein in step (e) the compacting is performed at a pressure of 75 to 300 MPa and the heating is carried out at a temperature of 725°-925° C. for a period of 2-16 hours.
14. The method of claim 12 , wherein the molybdenum powder has an average particle size of 20 microns or less.
15. The method of claim 12 , wherein the titanium powder has an average particle size of 40 to 150 microns.
16. The method of claim 12 , wherein the consolidating of step (c) is performed in a cold isostatic press.
17. The method of claim 12 , wherein the compacting/heating of step (e) is performed in a hot isostatic press.
18. The method of claim 12 , further comprising the steps of:
(f) removing a portion of the encapsulation on the first target plate;
(g) bonding the first target plate to a second MoTi target plate along an edge of the first and second plates to produce bonded plates;
and
(h) compacting while heating the bonded plates to produce a bonded target plate.
19. The method of claim 18 , wherein the bonded target plate is at least 55 inches by 67 inches in area.
20. The method of claim 18 , wherein the compacting and heating of step (h) is hot isostatic pressing carried out at a pressure of 75-175 MPa and a temperature of 700°-950° C.
21. The method of claim 12 , wherein said titanium powder is present in an amount of 40-60 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder.
22. The method of claim 12 , wherein said titanium powder is present in an amount of 50-60 atomic %, based on the total atomic % of the molybdenum and titanium powders, the balance being molybdenum powder.