Method and apparatus for dielectric etching during integrated circuit fabrication
A method for multi-step dielectric etching includes discharge steps between each of the etching steps in order to help release accumulated charge on the wafer produced by the previous etching step. The discharge steps stabilize the plasma discharge in each transition between etching steps. Charge elimination occurs because the negative species is relatively higher at the beginning of plasma spiking and can reach the wafer surface to reduce the accumulated charge.
1. A method for etching a multi-layered structure using a plasma reactor, comprising:
depositing a photoresist layer on top of the multi-layered dielectric structure;
flowing a first gas mixture into the plasma reactor and exciting the first gas mixture into a plasma capable of etching a first layer of the multi-layered dielectric structure;
etching the first layer using the plasma formed using the first gas mixture;
releasing an accumulated charge that results from the etching step performed on the first layer by applying a source power of constant magnitude to the plasma reactor before removing the photoresist layer;
flowing a second gas mixture into the plasma reactor and exciting the second gas mixture into a plasma capable of etching a second layer of the multi-layered dielectric structure; and
etching the second layer using plasma formed using the second gas mixture.
2. The method of claim 1 , further comprising photographically patterning the photoresist layer to form a mask aperture defining a structure to be etched in the multi-layered dielectric structure.
3. The method of claim 1 , further comprising releasing an accumulated charge that results from the etching step performed on the second layer by applying the source power of constant magnitude to the plasma reactor.
4. The method of claim 1 , further comprising:
flowing a third gas mixture into the plasma reactor and exciting the third gas mixture into a plasma capable of etching a third layer of the multilayer dielectric structure;
etching the third layer using the plasma formed using the third gas mixture; and
releasing an accumulated charge that results from the etching step performed on the third layer by applying the source power of constant magnitude to the plasma reactor.
5. The method of claim 1 , wherein the step of etching the first layer uses a gas mixture comprising Ar/CF 4 /C 4 F 8 /O 2 .
6. The method of claim 1 , wherein the step of releasing the charge accumulated during the step of etching the first layer uses an Ar gas.
7. The method of claim 1 , wherein the step of releasing the charge accumulated during the step of etching the first layer uses a release time of 5 seconds.
8. The method of claim 1 , wherein the step of releasing the charge accumulated during the step of etching the first layer uses a source power of 70 W and no bias power.
9. The method of claim 1 , wherein the step on etching the second layer uses a gas mixture comprising Ar/C 4 F 8 /CH 2 /F 2 /CO/O 2 .
10. The method of claim 1 , wherein the step of etching the second layer uses for 20 seconds.
11. The method of claim 3 , wherein the step of releasing the charge accumulated during the step of etching the second layer uses an Ar gas.
12. The method of claim 3 , wherein the step of releasing the charge accumulated during the step of etching the second layer uses a release time of 5 seconds.
13. The method of claim 3 , wherein the step of releasing the charge accumulated during the step of etching the second layer uses a source power of 70 W and no bias power.
14. The method of claim 4 , wherein the step of etching the third layer uses a gas mixture comprising Ar/CF 4 /O 2 .
15. The method of claim 4 , wherein the step of releasing the charge accumulated during the step of etching the third layer uses an Ar gas.
16. The method of claim 1 , further comprising limiting reflected power by holding a matching network constant at its most recent condition after the step of releasing the charge accumulated during the step of etching the first layer.
17. A method for etching a multi-layered dielectric structure having a photoresist mask using a plasma reactor comprising;
flowing a gas mixture into the plasma reactor and exciting the gas mixture into a plasma capable of etching the layer;
etching the layer using the plasma formed using the gas mixture; and
releasing an accumulated charge that results from the etching step performed on the layer using an inert gas for a certain release time and at a source power of constant magnitude to the plasma reactor before removing the photoresist mask.
18. The method of claim 17 , wherein the certain release time is 5 seconds.
19. The method of claim 17 , wherein the source power is 70 W, and wherein the release step does not use a bias power.
20. A method of claim 17 , wherein the inert gas comprises N 2 , He or Ar.