Tin-plated product and method for producing same
A tin-plated product formed by electroplating a substrate in a tin plating solution, which contains carbon particles and an aromatic carbonyl compound, to form a coating of a composite material, which contains the carbon particles in a tin layer, on the substrate has a coefficient of friction which is not greater than 0.18, preferably not greater than 0.13, with respect to the same kind of another tin-plated product, and has a glossiness of not less than 0.29 and a contact resistance of not greater than 1.0 mΩ. The coating has a thickness of 0.5 to 10 micrometers, and the content of carbon in the coating is in the range of from 0.1% by weight to 1.5% by weight. Separate protrusions containing the carbon particles are formed on the surface of the coating. The orientation plane of a tin matrix of the coating is (101) plane.
1 . A method for producing a tin-plated product, the method comprising the steps of:
adding carbon particles and an aromatic carbonyl compound to a tin plating solution; and
electroplating a substrate in the tin plating solution, which contains the carbon particles and the aromatic carbonyl compound, to form a coating of a composite material, which contains the carbon particles in a tin layer, on the substrate.
2 . A method for producing a tin-plated product as set forth in claim 1 , wherein said aromatic carbonyl compound is an aromatic aldehyde or an aromatic ketone.
3 . A tin-plated product comprising:
a substrate; and
a coating of a composite material which contains carbon particles in a tin layer, said coating being formed on said substrate,
wherein said tin-plated product has a coefficient of friction which is not greater than 0.18 with respect to the same kind of another tin-plated product as that thereof.
4 . A tin-plated product as set forth in claim 3 , wherein said coefficient of friction is not greater than 0.13.
5 . A tin-plated product as set forth in claim 3 , wherein said coating has a glossiness of not less than 0.29.
6 . A tin-plated product as set forth in claim 3 , wherein said coating has a thickness of 0.5 to 10 micrometers.
7 . A tin-plated product as set forth in claim 3 , wherein the content of carbon in said coating is in the range of from 0.1% by weight to 1.5% by weight.
8 . A tin-plated product as set forth in claim 3 , which has a contact resistance of not greater than 1.0 m Ω.
9 . A tin-plated product as set forth in claim 3 , wherein a plurality of protrusions spaced from each other are formed on a surface of said coating, and each of said protrusions contains said carbon particles.
10 . A tin-plated product as set forth in claim 3 , wherein an orientation plane of a tin matrix is (101) plane.
11 . A connecting terminal comprising:
a female terminal; and
a male terminal to be fitted into said female terminal,
wherein at least a part of at least one of said female and male terminals contacting the other terminal thereof is made of a tin-plated product as set forth in claim 3.