Techniques for the use of amorphous carbon (APF) for various etch and litho integration schemes
A method of etching a substrate is provided. The method of etching a substrate includes transferring a pattern into the substrate using a double patterned amorphous carbon layer on the substrate as a hardmask. Optionally, a non-carbon based layer is deposited on the amorphous carbon layer as a capping layer before the pattern is transferred into the substrate.
1. A method of etching a substrate layer, comprising:
depositing an amorphous carbon layer on a substrate layer overlying an underlayer;
defining a first feature pattern in the amorphous carbon layer;
depositing a layer of photoresist on the amorphous carbon layer;
patterning the photoresist;
transferring the pattern in the photoresist through the amorphous carbon layer to form a second feature pattern in the amorphous carbon layer; and
transferring the first and second feature patterns in the amorphous carbon layer through the substrate layer to provide first and second features in the substrate layer.
2. The method of claim 1 , wherein the amorphous carbon layer is deposited by vapor deposition from a gas mixture comprising propylene.
3. The method of claim 1 , wherein the substrate layer comprises a material selected from the group consisting of silicon, polysilicon, an oxide, a nitride, tungsten, tungsten silicide, aluminum, silicon oxycarbide, and combinations thereof.
4. The method of claim 1 , wherein the amorphous carbon layer is deposited at a power of between about 1 W/in 2 and about 100 W/in 2 .
5. The method of claim 1 , further comprising removing the amorphous carbon layer from the substrate layer after the first and second feature patterns in the amorphous carbon layer are transferred through the substrate layer.
6. The method of claim 1 , wherein the amorphous carbon layer is deposited by vapor deposition from a gas mixture comprising one or more hydrocarbons.
7. The method of claim 6 , wherein the gas mixture further comprises hydrogen.
8. The method of claim 6 , wherein the gas mixture further comprises argon.
9. A method of etching a substrate layer, comprising:
depositing an amorphous carbon layer on a substrate layer overlying an underlayer;
depositing a non-carbon based layer on the amorphous carbon layer;
defining a first feature pattern in the non-carbon based layer and in the amorphous carbon layer;
depositing a layer of photoresist on the non-carbon based layer after the first feature pattern is defined in the non-carbon based layer and in the amorphous carbon layer;
patterning the photoresist;
transferring the pattern in the photoresist through the non-carbon based layer and the amorphous carbon layer to form a second feature pattern in the amorphous carbon layer; and
transferring the first and second feature patterns in the amorphous carbon layer through the substrate layer to provide first and second features in the substrate layer.
10. The method of claim 9 , wherein the amorphous carbon layer is deposited by vapor deposition from a gas mixture comprising one or more hydrocarbons.
11. The method of claim 9 , wherein the substrate layer comprises a material selected from the group consisting of silicon, polysilicon, an oxide, a nitride, tungsten, tungsten silicide, aluminum, silicon oxycarbide, and combinations thereof.
12. The method of claim 9 , further comprising removing the amorphous carbon layer and the non-carbon based layer from the substrate layer after the first and second feature patterns in the amorphous carbon layer are transferred through the substrate layer.
13. The method of claim 9 , wherein the non-carbon based layer is selected from the group consisting of amorphous silicon, silicon nitride, silicon oxynitride, silicon oxide, doped silicon oxide, silicon oxycarbide, carbides, silicon carbide, titanium, and titanium nitride.
14. The method of claim 13 , wherein the non-carbon based layer has a thickness of between about 50 Å and about 500 Å.
15. A method of etching a substrate layer, comprising:
depositing an amorphous carbon layer on a substrate layer overlying an underlayer;
depositing an anti-reflective coating on the amorphous carbon layer;
defining a first feature pattern in the anti-reflective coating and in the amorphous carbon layer;
depositing a layer of photoresist on the anti-reflective coating after the first feature pattern is defined in the anti-reflective coating and in the amorphous carbon layer;
patterning the photoresist;
transferring the pattern in the photoresist through the anti-reflective coating and the amorphous carbon layer to form a second feature pattern in the amorphous carbon layer; and
transferring the first and second feature patterns in the amorphous carbon layer through the substrate layer to provide first and second features in the substrate layer.
16. The method of claim 15 , wherein the amorphous carbon layer is deposited by vapor deposition from a gas mixture comprising one or more hydrocarbons.
17. The method of claim 15 , wherein the substrate layer comprises a material selected from the group consisting of silicon, polysilicon, an oxide, a nitride, tungsten, tungsten silicide, aluminum, silicon oxycarbide, and combinations thereof.
18. The method of claim 15 , wherein the anti-reflective coating layer is a material selected from the group consisting of amorphous silicon, silicon nitride, silicon oxynitride, silicon oxide, doped silicon oxide, silicon oxycarbide, carbides, silicon carbide, titanium, and titanium nitride.
19. The method of claim 15 , wherein the amorphous carbon layer is deposited at a power of between about 1 W/in 2 and about 100 W/in 2 .
20. The method of claim 15 , wherein the amorphous carbon layer is deposited at a temperature of about 100° C. to about 700° C.