Oxygen-enriched niobium wire
View Patent ↗A process for providing a niobium wire and its use for connection to niobium or niobium oxide capacitors. The wire is enriched with oxygen and preferably has oxygen concentrations of about 3,000 to 30,000 μg/g.
1. A process for producing oxygen-enriched niobium wire, comprising the steps of: treating a niobium pre-wire in an oxygen-containing atmosphere in a closed chamber at an elevated temperature of 600-800° C. at a pressure below 5 mBars until the bulk of the niobium pre-wire is enriched with 3000 to 30,000 μg/g oxygen; and drawing the niobium treated in this way into wire.
2. A process in accordance with claim 1 , wherein the treating step is carried out in an atmosphere of air.
3. A process in accordance with claim 1 , wherein the drawing step includes drawing the niobium into wire having a diameter of 0.2-0.4 mm.
4. A process in accordance with claim 1 , wherein the drawing step is carried out at room temperature.