Coatings containing polysilazanes for metal and polymer surfaces
View Patent ↗The invention relates to the use of polysilazanes as a permanent coating on metal and polymer surfaces for preventing corrosion, increasing scratch resistance and to facilitate easier cleaning. The invention comprises a solution of a polysilazane or a blend of polysilazanes of the general formula 1 —(SiR′R″—NR′″) n — (1) where R′, R″ and R′″ are identical or different and independently of one another represent hydrogen or an optionally substituted alkyl, aryl, vinyl or (trialkoxysilyl)alkyl group and n represents a whole number and is calculated in such a way that the polysilazane has a numerical average molecular weight of 150 to 150 000 g/mol, in a solvent. The invention also relates to a method for producing the coating.
1. A coating solution for metal surfaces, polymers or coating systems, comprising a solution of a polysilazane or a mixture of polysilazanes of the formula 1
—(SiR′R″—NR′″) n — (1)
where R′, R″ and R′″ are identical or different and independently of one another are hydrogen or an unsubstituted or substituted alkyl, aryl, vinyl or (trialkoxysilyl)alkyl radical, n being an integer and having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150000 g/mol, in a solvent wherein the coating composition further comprises a binder and which further comprises inorganic nanoparticles.
2. The coating as claimed in claim 1 , wherein R′, R″ and R′″ independently of one another are a radical selected from the group of consisting of hydrogen, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, phenyl, vinyl 3-(triethoxysilyl)propyl and 3-(trimethoxysilylpropyl).
3. The coating as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes has at least one polysilazane of the formula (2)
—(SiR′R″—NR′″) n —(SiR*R**—NR***) p — (2)
where R′, R″, R′″, R*, R**, and R*** independently of one another are hydrogen or an unsubstituted or substituted alkyl, aryl, vinyl or (trialkoxysilyl)alkyl radical, n and p being an integer and n having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150000 g/mol.
4. The coating solution as claimed in claim 3 , wherein
R′, R′″ and R*** are hydrogen and R″, R* and R** are methyl;
R′, R′″ and R*** are hydrogen and R″ and R* are methyl and R** is vinyl; or
R′, R′″, R* and R*** are hydrogen and R″ and R** are methyl.
5. The coating solution as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes has at least one polysilazane of the formula (3)
—(SiR′R″—NR′″) n —(SiR*R**—NR***) p —(SiR 1 R 2 —NR 3 ) q — (3)
where R′, R″, R′″, R*, R**, R***, R 1 , R 2 and R 3 independently of one another are hydrogen or an unsubstituted or substituted alkyl, aryl, vinyl or (trialkoxysilyl)alkyl radical, n, p and q being integers and n having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150000 g/mol.
6. The coating solution as claimed in claim 5 , wherein R′, R′″ and R*** are hydrogen and R″, R*, R** and R 2 are methyl, R 3 is (triethoxysilyl)propyl and R 1 is alkyl or hydrogen.
7. The coating solution as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes contains 1% to 80% by weight of the polysilazane.
8. The coating solution as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes contains 0.001% to 10% by weight of at least one catalyst.
9. The coating solution as claimed in claim 8 , wherein the at least one catalyst is selected from the group consisting of organic amines, acids, metals, metal salts and mixtures thereof.
10. The coating solution as claimed in claim 8 , wherein the solvent is an anhydrous organic solvent containing no reactive groups.
11. The coating solution as claimed in claim 1 , where the binder is selected from a group consisting of cellulose ethers, cellulose esters, rubbers, rosins, amino resins, alkyd resins, acrylic resins, polyacrylates, polyesters, polyisocyanates, blocked polyisocyanates and polysiloxanes.
12. The permanent coating as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes contains 5% to 50% by weight of the polysilazane.
13. The permanent coating as claimed in claim 1 , wherein the solution of a polysilazane or a mixture of polysilazanes contains 10% to 40% by weight of the polysilazane.
14. The coating solution of claim 1 where the binder is polyacrylate.
15. An article with a metal surface, polymer surface or coating surface coated with a permanent coating as set forth in claim 1 .
16. The article as claimed in claim 15 , wherein the metal surface is selected from the group consisting of alloys of iron, steel, galvanized steel, aluminum, chromium, nickel, zinc, titanium, vanadium, molybdenum, magnesium and copper.
17. The article as claimed in claim 15 , wherein the polymer surface is selected from the group consisting of polycarbonate, polymethyl methacrylate, polyether ether ketone, polyethylene, polypropylene, polyamide and polyethylene terephthalate.
18. The article as claimed in claim 15 , wherein the coating surface is an acrylate-based, epoxy-based or urethane-based coating.
19. An article with a polymer surface coated with a coating solution comprising a solution of a polysilazane or a mixture of polysilazanes of the formula 1
—(SiR′R″—NR′″) n — (1)
where R′, R″ and R′″ are identical or different and independently of one another are hydrogen or an unsubstituted or substituted alkyl, arly, vinyl or (trialkoxysilyl)alkyl radical, n being an integer and having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150000 g/mol, in a solvent wherein the coating composition further comprises a binder and wherein the polymer surface is selected from the group consisting of polycarbonate, polymethyl methacrylate, polyether ether ketone, polyethylene, polypropylene, polyamide and polyethylene terephthalate and wherein the coating surface is an acrylate-based, epoxy-based or urethane-based coating.
20. An article with a coated surface coated with a coating solution comprising a solution of a polysilazane or a mixture of polysilazanes of the formula 1
—(SiR′R″—NR′″) n — (1)
where R′, R″ and R′″ are identical or different and independently of one another are hydrogen or an unsubstituted or substituted alkyl, arly, vinyl, or (trialkoxysilyl)alkyl radical, n being an integer and having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150000 g/mol, in a solvent wherein the coating composition further comprises a binder and wherein the coating surface is an acrylate-based, epoxy-based or urethane-based coating.
21. A method of producing a coating on a metal surface or a polymer surface, comprising the steps of applying a solution comprising a polysilazane or a mixture of polysilazanes of the formula (1)
—(SiR′R″—NR′″) n — (1)
where R′, R″ and R′″ are identical or different and independently of one another are hydrogen or an unsubstituted or substituted alkyl, aryl or (trialkoxysilyl)alkyl radical, n being an integer and having a value such that the polysilazane or mixture of polysilazanes has a number-average molecular weight of 150 to 150 000 g/mol, in a solvent to a metal surface to form a coating and curing the coating, wherein the solution further comprises a binder and which further comprises inorganic nanoparticles.