View Patent ↗An iridium alloy is produced having at least 85% by weight iridium, at least 0.005% by weight molybdenum, 0.001 to 0.6% by weight hafnium and, optionally, rhenium, the sum of molybdenum and hafnium being between 0.002 and 1.2% by weight. The iridium alloy is produced in a process, in which an IrMo and an IrHf master alloy, respectively, are created in an electric arc and immersed into an iridium melt, optionally together with Re.
1. An iridium alloy having improved creep resistance at 1800° C. and consisting essentially of at least 85% by weight iridium, at least 0.005% by weight molybdenum, 0.0005 to 0.6% by weight hafnium, and 0.1 to 5% by weight rhenium, the molybdenum and hafnium being present in the alloy in a total amount between 0.002 and 1.2% by weight.
2. The iridium alloy according to claim 1 , consisting essentially of at least 85% by weight iridium, 0.1 to 5% by weight rhenium, 0.01 to 0.8% by weight molybdenum and 0.002 to 0.4% by weight hafnium.
3. The iridium alloy according to claim 1 , wherein the amount of molybdenum is 0.02 to 0.3% by weight.
4. The iridium alloy according to claim 1 , wherein the amount of hafnium is 0.002 to 0.2% by weight.
5. A process for production of the iridium alloy according to claim 1 , comprising producing a master alloy of Ir Mo and a master alloy of Ir Hf in an electric arc and immersing each of the master alloys into an iridium melt, with Re.
6. A crucible, bath or glass working tool comprising the iridium alloy according to claim 1 .
7. A method for growing crystals of high melting oxidic melts, wherein the crystals are grown in a crucible according to claim 6 .
8. The method according to claim 7 , wherein the crystals are selected from aluminium oxide and neodymium yttrium aluminum garnet.
9. A method for manufacturing high melting of glass, wherein the manufacturing takes place in the crucible, bath or glass processing tool according to claim 6 .