Method of recovering silver using anion-exchange resin
View Patent ↗The present invention provides a method of recovering silver safely and efficiently from a chloride or bromide bath containing various metals. Specifically, a method of recovering silver from a hydrochloric acid solution containing alkali and/or alkaline earth metal chloride, silver, copper and iron ions, comprising the steps of: (1) bringing the solution into contact with a strong-base anion-exchange resin to adsorb silver, copper, and iron on the anion-exchange resin; (2) then washing the anion-exchange resin with water to remove the adsorbed copper and iron; and (3) then bringing the ion-exchange resin into contact with a hydrochloric acid solution to elute the adsorbed silver, is provided.
1. A method of recovering silver from a hydrochloric acid solution containing alkali and/or alkaline earth metal chloride, silver, copper and iron ions, comprising the steps of:
(1) bringing the solution into contact with a strong-base anion-exchange resin to adsorb silver, copper, and iron on the anion-exchange resin;
(2) then washing the anion-exchange resin with water to remove the adsorbed copper and iron; and
(3) then bringing the ion-exchange resin into contact with a hydrochloric acid solution to elute the adsorbed silver.
2. The method according to claim 1 , wherein the concentration of silver in the acidic solution is not more than 30 mg/L,
in step (1), the bed volume BV is 10-20 and the space velocity SV is 5 or less;
in step (2), the bed volume BV is 7.5 or more and the space velocity SV is 5 or less; and
in step (3), the bed volume BV is 10 or more and the space velocity SV is 5 or less.
3. The method according to any one of claim to 2 , wherein the chlorine concentration in the acidic solution is 160 g/L to 200 g/L.
4. The method according to claim 2 , wherein the pH of the acidic solution ranges from 0.01 to 1.2.
5. The method according to claim 2 , wherein part of the copper is recovered in advance from the acidic solution by solvent extraction.
6. The method according to claim 1 , wherein the chlorine concentration in the acidic solution is 160 g/L to 200 g/L.
7. The method according to claim 6 , wherein the pH of the acidic solution ranges from 0.01 to 1.2.
8. The method according to claim 6 , wherein part of the copper is recovered in advance from the acidic solution by solvent extraction.
9. The method according to claim 1 , wherein the pH of the acidic solution ranges from 0.01 to 1.2.
10. The method according to claim 9 , wherein part of the copper is recovered in advance from the acidic solution by solvent extraction.
11. The method according to claim 1 , wherein part of the copper is recovered in advance from the acidic solution by solvent extraction.
12. The method according to claim 11 , wherein the acidic solution is oxidized prior to the solvent extraction to oxidize at least part of cuprous ions to cupric ions.
13. The method according to claim 1 , wherein the acidic solution is a leachate solution obtained by leaching copper ore or copper concentrate with a leach solution containing cupric chloride and/or ferric chloride, followed by solid-liquid separation.
14. The method according to claim 1 , wherein the acidic solution further contains alkali metal and/or alkaline earth metal bromide.
15. A method of recovering silver from a hydrochloric acid solution containing alkali and/or alkaline earth metal chloride, silver, copper and iron ions, and further containing at least one ion selected from the group consisting of zinc, silicon, aluminum, calcium, magnesium, and cobalt, comprising the steps of:
(1) bringing the solution into contact with a strong-base anion-exchange resin to adsorb silver, copper and iron on the anion-exchange resin, and when zinc is present, the zinc is adsorbed on the anion-exchange resin;
(2) then washing the anion-exchange resin with water to remove the adsorbed copper, iron, and zinc; and
(3) then bringing the ion-exchange resin into contact with a hydrochloric acid solution to elute the adsorbed silver.
16. The method according to claim 15 , wherein the concentration of silver in the acidic solution is not more than 30 mg/L,
in step (1), the bed volume BV is 10-20 and the space velocity SV is 5 or less;
in step (2), the bed volume BV is 7.5 or more and the space velocity SV is 5 or less; and
in step (3), the bed volume BV is 10 or more and the space velocity SV is 5 or less.
17. The method according to any one of claim to 15 , wherein the chlorine concentration in the acidic solution is 160 g/L to 200 g/L.
18. The method according to claim 15 , wherein the pH of the acidic solution ranges from 0.01 to 1.2.
19. The method according to claim 15 , wherein part of the copper is recovered in advance from the acidic solution by solvent extraction.
20. The method according to claim 15 , wherein the acidic solution is oxidized prior to the solvent extraction to oxidize at least part of cuprous ions to cupric ions.