Method of manufacturing a chemical mechanical polishing pad

1. A method of manufacturing a chemical mechanical polishing pad, comprising:

providing a polishing layer;

providing a chemical mechanical polishing pad manufacturing assembly, comprising:

a subpad layer having a top surface, a bottom surface and at least two wrap around tabs; a backing plate having a top side and a bottom side; a sacrificial layer having at least two recessed areas designed to facilitate attachment of the subpad layer to the backing plate; an unset reactive hot melt adhesive applied to the top surface of the subpad layer, wherein the unset reactive hot melt adhesive is applied in a pattern of parallel lines; wherein the subpad layer is disposed on the top side of the backing plate and the sacrificial layer is disposed on the bottom side of the backing plate, and wherein the at least two wrap around tabs extend to the bottom side of the backing plate;

stacking the polishing layer and the chemical mechanical polishing pad manufacturing assembly with the unset reactive hot melt adhesive interposed between the polishing layer and the subpad layer forming a stack;

applying an axial force to the stack;

allowing the unset reactive hot melt adhesive to set forming a reactive hot melt adhesive bond between the subpad layer and the polishing layer;

separating the at least two wrap around tabs from the subpad layer;

removing the sacrificial layer; and,

removing the subpad layer with the polishing layer bonded thereto from the backing plate.

2. The method of claim 1 , wherein the unset reactive hot melt adhesive is applied to the top surface of the subpad layer at a coat weight of 6,500 to 13,940 g/cm 2 .

3. The method of claim 1 , wherein the unset reactive hot melt adhesive is applied to the top surface of the subpad layer at a coat weight of 8,350 to 12,100 g/cm 2 .

4. The method of claim 1 , wherein the reactive hot melt adhesive is applied to the top surface of the subpad layer in a pattern of parallel lines, wherein the individual lines exhibit a thickness of 0.05 to 0.20 mm, a width of 1.5 to 3.25 mm and a spacing between individual lines of 1.5 to 3.25 mm.

5. The method of claim 1 , wherein the reactive hot melt adhesive is applied to the top surface of the subpad layer in a pattern of parallel lines, wherein the individual lines exhibit a thickness of 0.0762 to 0.172 mm, a width of 1.58 to 3.18 mm and a spacing between individual lines of 1.58 to 3.18 mm.

6. The method of claim 1 , wherein there are valleys that are not devoid of unset reactive hotmelt adhesive between the individual lines in the pattern of parallel lines, wherein a thickness of the unset reactive hot melt adhesive measured at a center of the valleys is ≦5% of a thickness of the unset reactive hot melt adhesive measured at a center of the individual lines.