Composite membranes with performance enhancing layers
View Patent ↗A composite membrane includes a filtration membrane with a surface; and a layer on the surface of the filtration membrane. The layer includes a polymer including a poly(ethylene glycol) moiety cross-linked with an ammonium salt or a precursor of an ammonium salt.
1. A method for making a composite membrane, comprising:
applying a coating composition to a surface of a filtration membrane, wherein the coating composition comprises:
a hydrophilic compound (A) selected from at least one of PEG-methacrylates, PEG-acrylates, PEG-diacrylate, PEG-dimethacrylate, or PEG-diepoxides;
a polymerizable compound (B) selected from monomers with the formula [(RNR 1 R 2 R 3 ) + X − ], wherein R is a (meth)acryl functional group, N is nitrogen, R 1 -R 3 , which may be the same or different, may be hydrogen or alkyl, and X is a halide, wherein the ratio by weight of the compound (A) to the compound (B) is about 1:1 to about 3:1; and
about 50 wt % to about 80 wt % water; and
curing the composition to form a layer on the membrane.
2. The method of claim 1 , wherein the filtration membrane is selected from the group consisting of microfiltration (MF), ultrafiltration (UF), nanofilitration (NF), reverse osmosis (RO), forward osmosis (FO) membranes, and combinations thereof.
3. The method of claim 1 , wherein the layer has a dry thickness of about 50 nm to about 5 μm.
4. The method of claim 1 , wherein the compound (A) is PEG-diacrylate.
5. The method of claim 1 , wherein the compound (B) is selected from the group consisting of 2-aminoethyl methacrylate hydrochloride, 2-dimethylaminoethyl methacrylate hydrochloride, dimethylaminoethyl methacrylate-methyl chloride and combinations thereof.
6. The method of claim 1 , wherein the coating composition further comprises a photoinitator.
7. The method of claim 6 , wherein the coating composition is cured with UV light.
8. A composite membrane comprising:
a filtration membrane selected from the group consisting of microfiltration (MF), ultrafiltration (UF), nanofilitration (NF), reverse osmosis (RO), forward osmosis (FO), and combinations thereof;
a layer on the membrane, wherein the layer comprises the cured reaction product of:
a hydrophilic compound (A) selected from at least one of PEG-methacrylates, PEG-acrylates, PEG-diacrylate, PEG-dimethacrylate, or PEG-diepoxides;
a polymerizable compound (B) selected from monomers with the formula [(RNR 1 R 2 R 3 ) + X − ], wherein R is a (meth)acryl functional group, N is nitrogen, R 1 -R 3 , which may be the same or different, may be hydrogen or alkyl, and X is a halide, wherein the ratio by weight of the compound (A) to the compound (B) is about 1:1 to about 3:1; and
about 50 wt % to about 80 wt % water.
9. The composite membrane of claim 8 , wherein the compound (A) is PEG diacrylate.
10. The composite membrane of claim 8 , wherein compound (B) is selected from the group consisting of 2-aminoethyl methacrylate hydrochloride, 2-dimethylaminoethyl methacrylate hydrochloride, dimethylaminoethyl methacrylate-methyl chloride and combinations thereof.
11. The composite membrane of claim 8 , wherein the layer has a dry thickness of about 50 nm to about 5 μm.