Substrate processing method and substrate processing apparatus
Provided is a substrate processing method comprising: loading a substrate, on which polysilazane is applied, into a substrate process chamber; maintaining an inside of the substrate process chamber, into which the substrate is loaded, in water vapor atmosphere and depressurization atmosphere at a temperature of 400° C.; performing a first heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in the water vapor atmosphere and the depressurization atmosphere at the temperature of 400° C.; next, increasing an inner temperature of the substrate process chamber from the temperature of 400° C. in the first heat treatment process to a temperature ranging from 900° C. to 1000° C.; and performing a second heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in water vapor atmosphere and depressurization atmosphere at the temperature ranging from 900° C. to 1000° C.
1. A substrate processing method comprising:
loading a substrate, on which polysilazane is applied, into a substrate process chamber;
maintaining an inside of the substrate process chamber, into which the substrate is loaded, in water vapor atmosphere and depressurization atmosphere at a temperature ranging from 350° C. to 450° C.;
performing a first heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in the water vapor atmosphere and the depressurization atmosphere at the temperature ranging from 350° C. to 450° C.;
next, increasing an inner temperature of the substrate process chamber from the temperature ranging from 350° C. to 450° C. in the first heat treatment process to a temperature ranging from 900° C. to 1000° C.; and
performing a second heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in water vapor atmosphere and depressurization atmosphere at the temperature ranging from 900° C. to 1000° C.
2. The substrate processing method of claim 1 , comprising, after the second heat treatment process, performing a third heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in inert gas atmosphere and depressurization atmosphere at the temperature ranging from 900° C. to 1000° C.
3. The substrate processing method of claim 1 , wherein, before applying the polysilazane, a silicon nitride film is formed on the substrate.
4. A substrate processing apparatus comprising:
a substrate process chamber configured to accommodate a substrate;
a heater configured to heat the substrate accommodated in the substrate process chamber;
a water vapor generator;
a water vapor supply pipe configured to supply water vapor from the water vapor generator into the substrate process chamber;
an exhaust pipe configured to exhaust atmosphere in the substrate process chamber; and
a control part,
wherein the control part executes a control to perform a first heat treatment process on the substrate in a state where an inside of the substrate process chamber is maintained in water vapor atmosphere and depressurization atmosphere at a temperature ranging from 350° C. to 450° C.; to increase an inner temperature of the substrate process chamber from the temperature ranging from 350° C. to 450° C. in the first heat treatment process to a temperature ranging from 900° C. to 1000° C.; to perform a second heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in water vapor atmosphere and depressurization atmosphere at the temperature ranging from 900° C. to 1000° C.; and then, to perform a third heat treatment process on the substrate in a state where the inside of the substrate process chamber is maintained in inert gas atmosphere and depressurization atmosphere at the temperature ranging from 900° C. to 1000° C.